Due to huge uncertainties in the geometric dimensions of atomic force microscopy (AFM) probes, samples’ rheological properties and lateral forces are difficult to measure and compare quantitatively. Hence, mathematical calibration methods fail to calibrate AFM probes accurately. To solve this problem, we will introduce in this paper “blind calibration methods” to determine quantitatively lateral forces, elastic constants and viscosity. For lateral force, a geometry factor is used to calibrate any cantilever using this “blind method”. The essential part of this method is a calibration standard sample that is commercially available. We have chosen silicon for our calibration standard sample and will discuss a cleaning procedure for reproducible lateral force measurements. We will provide an absolute friction value, which will serve as one of three parameters necessary to obtain the geometry factor. The other two components being the normal spring constant and the relative friction signal measured with the cantilever of interest. Further, we will discuss force modulation measurements and the problems that occur around resonances. We will provide a procedure to determine elastic constants also based on the silicon calibration standard. Finally, the “blind calibration method” will also be used to achieve kinematic viscosity values.

Extracellular matrix (ECM) proteins play an essential role during biomineralization in bone and engineered tissues. In a previous study ([1]), we showed that calcite preferentially nucleated on pure elastin fibers. However, the actual cellular ECM fibers are composed of a combination of proteins, primarily collagen, fibronectin and some elastin. Here we follow the calcium carbonate- and calcium phosphate- mineralization process in vitro when these ECM proteins are combined and determine the differences between these proteins in the biomineralization process. The surface morphology and mechanical properties of the protein fibers during the early stages were probed by atomic force microscopy (AFM) and shear modulation force microscopy (SMFM). The nucleation of the mineral crystals on the protein matrices was investigated by scanning electron microscopy (SEM). Preliminary data showed that the moduli of all protein fibers increased at the early stages, with collagen having the largest increase in supersaturated calcium bicarbonate solution. In metastable calcium phosphate solutions the modulus of the mixed elastin-fibronectin fibres increased to a greater extent than the moduli of the fibers composed of the single proteins. Longer exposure in the mineral solutions led to the formation of crystals templated along the self-assembled fiber structures.

To successfully induce tissue repair or regeneration in vivo, bioengineered constructs must possess both optimal bioactivity and mechanical strength. This is because cell interaction with the extracellular matrix (ECM) produces two different but concurrent signaling mechanisms: ligation-induced signaling, which depends on ECM biological stimuli, and traction-induced signaling, which depends on ECM mechanical stimuli. In this report, we provide a fundamental understanding of how alterations in mechanical stimuli alone, produced by varying the viscoelastic properties of our bioengineered construct, modulate phenotypic behavior at the whole-cell level. Using a physiologically relevant ECM mimic composed of hyaluronan and fibronectin, we found that adult human dermal fibroblasts modify their mechanical response in order to match substrate stiffness. More specifically, the cells on stiffer substrates had higher modulus and a more stretched and organized actin cytoskeleton (and vice versa), which translated into larger traction forces exerted on the substrate. This modulation of cellular mechanics had contrasting effects on migration and proliferation, where cells migrated faster on softer substrates while proliferating preferentially on the stiffer ones. These findings implicate substrate rigidity as a critical design parameter in the development of bioengineered constructs aimed at eliciting maximal cell and tissue function.

Understanding how biomineralization occurs in the extracellular matrix (ECM) of bone cells is crucial to the development of a successfully engineered bone tissue scaffold, and to date there has not been a well-established method for the quantitative examination of bone mineralization in situ. We investigated the mechanical properties of MC3T3-E1 osteoblast-like cells and the crystalline properties of their biomineralized ECM in vitro using shear modulation force microscopy (SMFM), confocal laser scanning microscopy (CLSM), synchrotron X-ray diffraction (XRD), and Fourier-transform infrared spectroscopy (FTIR). The elastic modulus of the mineralizing cells increased at time points corresponding to mineral production, whereas that of the non-mineralizing cells did not vary significantly over time. CLSM showed a restructuring of the F-actin fiber network of mineralizing cells with time, which indicates remodeling activities in the cytoskeleton and was not seen in the non-mineralizing cells. Both XRD and FTIR showed that the mineralizing subclone produced hydroxyapatite in situ and that the non-mineralizing subclone was in fact weakly biomineralizing.

Electrospinning has been emerging as one of the most efficient methods to fabricate polymer nanofibers. In this paper, PS/clay nanocomposite fibers with varying diameters were electrospun onto solid substrates. The fiber diameters were adjusted from 4 microm to 150 nm by changing the solution concentration. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), and atomic force microscopy (AFM) were used to characterize the fiber morphology. Shear modulation force microscopy (SMFM) was utilized to investigate the surface nanomechanical properties of electrospun fibers as a function of the fiber diameter and temperature. In the absence of clay, no change in T(g) was observed, even though a large increase of shear modulus below the glass transition temperature was found. This effect was postulated to result from the molecular chain alignment during electrospinning. The addition of functionalized clays to the spinning solution produced fibers with a highly aligned montmorillonite layer structure at a clay concentration of 4 wt %. Clay agglomerates were observed at higher concentrations. The existence of clay further enhanced the shear modulus of fibers and increased the glass transition temperature by nearly 20 degrees C.

Silicon carbide was successfully deposited onto a heated HK40 substrate. An array of characterization techniques (scanning electron microscopy, atomic force microscopy, and scratch tests) demonstrated that the processing conditions were suitable for good coverage and promising adhesion behavior.