The purpose of this study is to find a direct and quantitative correlation of the structure of Co3-xFexO4 nanoparticles with catalytic performance in 2-propanol oxidation. Eight nanocrystalline samples with varying iron contents arc synthesized, and quantitative information regarding their structure is obtained from nitrogen physisorption, X-ray diffraction (XRD), X-ray absorption near-edge structure (XANES), and extended X-ray absorption line structure (EXAFS) analyzed by reverse Monte Carlo simulations. The catalytic performance is tested in 2-propanol oxidation in the gas phase. Overall, catalytic conversion data as a function of temperature are deconvoluted to obtain conversion and half-conversion temperatures as quantitative parameters for the different catalytic reaction channels. The crystal structure is described by a spinel structure with interstitial cation defects. These defects result in a reduced electronic state of the nanoparticles. The defect density depends on the cationic composition. We also observe a complex cationic distribution on tetrahedral and octahedral sites, which is strongly influenced by the overall cationic composition. In the catalytic tests, the samples exhibit a low-temperature pathway, which is deactivated in subsequent runs but can be recovered by an oxidative treatment of the catalyst. We find that the frequency of cation pairs Co-O-Co-O and Co-O-Co-T of the individual samples correlates directly to their catalytic activity and selectivity.

Co3O4 nanospheres with a preferential (110) surface orientation showed excellent catalytic properties in the selective gas-phase oxidation of 2-propanol. A preferential Mars–van Krevelen mechanism on the Co3O4(110) surface was identified by DFT + U.

Crystalline Co3O4 nanoparticles with a uniform size of 9 nm as shown by X-ray diffraction (XRD) and transmission electron microscopy (TEM) were synthesized by thermal decomposition of cobalt acetylacetonate in oleylamine and applied in the oxidation of 2-propanol after calcination. The catalytic properties were derived under continuous flow conditions as a function of temperature up to 573 K in a fixed-bed reactor at atmospheric pressure. Temperature-programmed oxidation, desorption (TPD), surface reaction (TPSR), and 2-propanol decomposition experiments were performed to study the interaction of 2-propanol and O-2 with the exposed spinel surfaces. Co3O4 selectively catalyzes the oxidative dehydrogenation of 2-propanol, yielding acetone and H2O and only to a minor extent the total oxidation to CO2 and H2O at higher temperatures. The high catalytic activity of Co3O4 reaching nearly full conversion with 100% selectivity to acetone at 430 K is attributed to the high amount of active Co3+ species at the catalyst surface as well as surface-bound reactive oxygen species observed in the O-2 TPD, 2-propanol TPD, TPSR, and 2-propanol decomposition experiments. Density functional theory calculations with a Hubbard U term support the identification of the 5-fold-coordinated octahedral surface Co-5c(3+) as the active site, and oxidative dehydrogenation involving adsorbed atomic oxygen was found to be the energetically most favored pathway. The consumption of surface oxygen and reduction of Co3+ to Co2+ during 2-propanol oxidation derived from X-ray absorption spectroscopy and X-ray photoelectron spectroscopy measurements before and after reaction and poisoning by strongly bound carbonaceous species result in the loss of the low-temperature activity, while the high-temperature reaction pathway remained unaffected.

CoFe2O4 nanoparticles (NPs) were synthesized by using a colloidal one-pot synthesis method based on the decomposition of metal acetylacetonates in the presence of oleyl amine. The characterization by X-ray diffraction, transmission electron microscopy and N-2 physisorption revealed non-porous spinel phase CoFe2O4 NPs with an average particle size of 4 nm. The unsupported metal oxide NPs were applied in the selective oxidation of 2-propanol in a continuously operated fixed-bed reactor under quasi steady-state conditions using a heating rate of 0.5 k min(-1). 2-Propanol was found to be oxidatively dehydrogenated over CoFe2O4 yielding acetone and H2O with high selectivity. Only to a minor extent dehydration to propene and total oxidation to CO2 was observed at higher temperatures. The detected low-temperature reaction pathway with maxima at 430 and 510 K was inhibited after the initial 2-propanol oxidation up to 573 K, but an oxidative treatment in O-2 or N2O atmosphere led to full regeneration. No correlation between the desorbing amount or the surface oxygen species investigated by O-2 temperature programmed desorption experiments and the low-temperature activity was observed. The amounts of evolving CO2 during the TPO experiments indicate deactivation due to formation of carbonaceous species. Inhibition experiments with pre-adsorbed reaction intermediates and infrared spectroscopy identified acetate species as reversible poison, whereas carbonates are rather spectators. In addition, carbon deposition was detected by X-ray photoelectron spectroscopy, which also revealed a minor influence of cobalt reduction during the deactivation process as confirmed by X-ray absorption spectroscopy studies. (C) 2019 Elsevier Inc. All rights reserved.

Monocrystalline, yet porous mosaic platelets of cobalt ferrite, CoFe2O4, can be synthesized from a layered double hydroxide (LDH) precursor by thermal decomposition. Using an equimolar mixture of Fe2+, Co2+, and Fe3+ during co-precipitation, a mixture of LDH, ((FeCoII)-Co-II)(2/3)Fe-1/3(III)(OH)(2)(CO3)(1/6)mH(2)O, and the target spinel CoFe2O4 can be obtained in the precursor. During calcination, the remaining Fe-II fraction of the LDH is oxidized to Fe-III leading to an overall Co2+:Fe3+ ratio of 1:2 as required for spinel crystallization. This pre-adjustment of the spinel composition in the LDH precursor suggests a topotactic crystallization of cobalt ferrite and yields phase pure spinel in unusual anisotropic platelet morphology. The preferred topotactic relationship in most particles is [111](Spinel)vertical bar[001](LDH). Due to the anion decomposition, holes are formed throughout the quasi monocrystalline platelets. This synthesis approach can be used for different ferrites and the unique microstructure leads to unusual chemical properties as shown by the application of the ex-LDH cobalt ferrite as catalyst in the selective oxidation of 2-propanol. Compared to commercial cobalt ferrite, which mainly catalyzes the oxidative dehydrogenation to acetone, the main reaction over the novel ex-LDH cobalt is dehydration to propene. Moreover, the oxygen evolution reaction (OER) activity of the ex-LDH catalyst was markedly higher compared to the commercial material.