Spin-crossover (SCO) nanoparticles (NPs) of the ID coordination polymer [Fe-(HTrz)2(Trz)]·(BF4), where HTrz = 1H-1,2,4-triazole, have been synthesized with integrated luminescence properties, focusing on the role of dopant trivalent Terbium (Tb) ions. Using a reverse micelle method, three types of nanoparticles were synthesized: pristine NPs (NP1), silica covered (NP2), and Tb-doped (NP3) NPs. Structural and morphological analyses, including TEM, STEM-XEDS, FT-IR, P-XRD, XPS, and XAFS spectroscopy, confirmed the successful incorporation of Tb ions into the silica matrix of NP3 and revealed their bonding environment with SiO4 tetrahedra and nitrate ions. Magnetic susceptibility measurements demonstrated hysteretic SCO behavior in all nanoparticle types, with NP3 exhibiting the highest thermal hysteresis width and a shift in critical temperatures, indicating enhanced cooperativity and modified magnetic properties due to the presence of Tb ions. Temperature-dependent photoluminescence (PL) measurements of NP3 showed hysteresis during thermal cycling, attributed to SCO transitions between high- and low-spin states. The study highlights the synergy between SCO and luminescence properties, paving the way for the development of multifunctional materials for applications in optoelectronics, sensors, and thermometry. These findings provide valuable insights into the design and optimization of advanced SCO-luminescent nanomaterials.

Experimental protocols based on Electron Paramagnetic Resonance (EPR) and Raman spectroscopy are presented for the investigation of the Fe(II) spin transition in Cu(II)-doped 1-D spin-crossover (SCO) nanoparticles of the type [Fe1−xCux(NH2trz)3]Br2 where x = 0.03 and 0.06 and NH2trz = 4-amino-1, 2, 4-triazole. The resulting nanoparticles were characterized using Transmission Electron Microscopy (TEM), Infrared (IR) spectroscopy, and powder X-ray diffraction (p-XRD). Magnetic susceptibility measurements revealed a dependence on the scan rate, with critical temperatures and hysteresis widths varying accordingly. EPR spectroscopy provided insights into the doped nanoparticles’ structural changes and spin-state transitions. The Cu(II) dopants exhibited significant g-factor anisotropy and hyperfine structure, indicative of a distorted octahedral coordination. The EPR spectra indicated that the spin transition occurs in domains populated by ions of the same spin state. Cu(II) ions show different spectral characteristics depending on whether they are in high-spin or low-spin domains of Fe(II). Changes in Raman bands induced by laser power reveal structural and electronic rearrangements during the LS to HS transition. The findings provide insights into metal–ligand interactions and the molecular mechanisms underlying the SCO process.

We report the controlled synthesis of samarium-iron Prussian blue analogues (SmFe PBAs) with novel morphologies, achieved through a systematic reverse micelle strategy using the non-ionic surfactant Triton X-100. By varying key experimental parameters-such as the water-to-surfactant molar ratio (ω0), the concentration of TX-100, and the volumetric ratio of cyclohexane to surfactant-we obtained a diverse range of particle shapes, including unprecedented daisy-like architectures with 4, 5, and 6 petals. These morphologies emerge within a narrow compositional window, implicating the formation of reverse bilayer vesicles as transient templates during nucleation and growth. Detailed morphological and structural characterization (TEM, SEM, XPS, PXRD, IR spectroscopy) revealed size-tunable particles ranging from 250 nm to 7 μm, while silica coating was achieved via a two-step sol-gel route enabling further miniaturization. Magnetic measurements highlight a strong size- and shape-dependent variation in coercive field (Hc), reaching up to 3320 Oe in submicron particles-among the highest reported for SmFe PBAs-attributed primarily to enhanced shape anisotropy. Our findings provide new insights into PBAs' morphology-property relationships and open pathways toward engineering anisotropic magnetic nanomaterials through soft templating in reverse micellar systems.

Stable aqueous dispersions of spin-crossover (SCO) doped [FeII(Htrz)2(trz)](BF4) nanoparticles (NPs) were prepared by using water-soluble polyvinylpyrrolidone (PVP) as protecting polymer. The metal or ligand substitution percentage regulated the ultra-small size and morphology of the NPs. At the same time, the colloidal dispersions showed a complete conversion of the LS state to the HS state of the FeII ion. An effective experimental method is presented for preparing PVP-coated NPs presenting stable aqueous colloidal dispersions and hysteretic SCO behavior close to RT, which is essential for future drug delivery and MRI-bioimaging perspectives.

Trivalent lanthanide ions have emerged as promising candidates for precise and remote temperature sensing. Among them, Pr3+-based luminescent thermometers remain underexplored, particularly those operating in the near-infrared (NIR) spectral region. This work presents the synthesis and thorough characterization of a novel Pr3+-based coordination polymer, {[Pr2 IIIPt3 II(CN)12(4,4 '-bpyO2)4(H2O)6]4H2O}n (1), as a rare example of Pr3+ luminescent thermometry. Coordination between Pr3+ ions, cyanido-bridged Pt2+ centers, and 4,4 '-bpyO2 ligands enables efficient energy transfer, producing luminescence in visible and near-infrared regions. The polymer demonstrates distinct temperature-dependent luminescence over a wide range (12-386 K), with relative thermal sensitivities of congruent to 1%K-1 and a minimum temperature uncertainty of 0.2 K.

Surface-Enhanced Raman Spectroscopy (SERS) is a powerful, non-destructive technique for enhancing molecular spectra, first discovered in 1974. This study investigates the enhancement of Raman signals from single- and few-layer molybdenum disulfide (MoS2) when interacting with silver nanoparticles. We synthesized a MoS2 membrane primarily consisting of monolayers and bilayers through a wet chemical vapor deposition method using metal salts. The silver nanoparticles were either directly grown on the MoS2 membrane or placed beneath it. Raman measurements revealed a significant increase in signal intensity from the MoS2 membrane on the silver nanoparticles, attributed to localized surface plasmon resonances that facilitate SERS. Our results indicate that dichalcogenide/plasmonic systems have promising applications in the semiconductor industry.

A synthetically controllable two-step spin transition was observed in iron(II) spin crossover nanoparticles of the dehydrated one-dimensional coordination polymer [Fe(NH2trz)3]Br2 (NH2trz = 4-amino-1,2,4-triazole) using the reverse micellar method. The change from two-step to one-step hysteretic characteristics succeeded by changing the reaction time.

A facile experimental protocol for the synthesis of poly(ethylene glycol)-modified (PEGylated) gold nanorods (AuNRs@PEG) is presented as well as an effective drug loading procedure using the non-steroidal anti-inflammatory drug (NSAID) naproxen (NAP). The interaction of AuNRs@PEG and drug-loaded AuNRs (AuNRs@PEG@NAP) with calf-thymus DNA was studied at a diverse temperature revealing different interaction modes; AuNRs@PEG may interact via groove-binding and AuNRs@PEG@NAP may intercalate to DNA-bases. The cleavage activity of the gold nanoparticles for supercoiled circular pBR322 plasmid DNA was studied by gel electrophoresis while their affinity for human and bovine serum albumins was also evaluated. Drug-release studies revealed a pH-sensitive behavior with a release up to a maximum of 24% and 33% NAP within the first 180 min at pH = 4.2 and 6.8, respectively. The cytotoxicity of AuNRs@PEG and AuNRs@PEG@NAP was evaluated against MCF-7 and MDA-MB-231 breast cancer cell lines. The development of AuNRs as an efficient non-steroidal anti-inflammatory drugs (NSAIDs) delivery system for chemotherapy is still in its infancy. The present work can shed light and inspire other research groups to work in this direction.

A novel experimental protocol based on a reverse micellar method is presented for the synthesis of graphene oxide (GO)-based hybrids with spin crossover nanoparticles (SCO NPs) of the 1D iron(II) coordination polymer with the formula [Fe(NH2trz)3](Br2). By introducing different quantities of 0.5% and 1.0% of GO (according to iron(II)) into the aqueous phase, two hybrids, NP4 and NP5, were synthesized, respectively. The morphological homogeneity of the NPs on the surface of the GO flakes is greatly improved in comparison to the pristine [Fe(NH2trz)3](Br2) NPs. From the magnetic point of view and at a low magnetic sweep rate of 1 K/min, a two-step hysteretic behavior is observed for NP4 and NP5, where the onset of the low-temperature second step appeared at 40% and 30% of the HS fraction, respectively. For faster sweep rates of 5–10 K/min, the two steps from the cooling branch are progressively smeared out, and the critical temperatures observed are T1/2↑ = 343 K and T1/2↓ = 288 K, with a thermal width of 55 K for both NP4 and NP5. A Raman laser power-assisted protocol was used to monitor the thermal tolerance of the hybrids, while XPS analysis revealed electronic interactions between the SCO NPs and the GO flakes.

A nanocomposite based on silica-coated AuNRs with the aminated silica-covered spin-crossover nanoparticles (SCO NPs) of the 1D iron(II) coordination polymer with the formula [Fe(Htrz)2(trz)](BF4) is presented. For the synthesis of the SCO NPs, the reverse micelle method was used, while the gold nanorods (AuNRs) were prepared with the aspect ratio AR = 6.0 using the seeded-growth method and a binary surfactant mixture composed of cetyltrimethylammonium bromide (CTAB) and sodium oleate (NaOL). The final nanocomposite was prepared using the heteroaggregation method of combining different amounts of SCO NPs with the AuNRs. The nonlinear optical (NLO) properties of the hybrid AuNRs coated with different amounts of SCO NPs were studied in detail by means of the Z-scan technique, revealing that the third-order NLO properties of the AuNRs@SCO are dependent on the amount of SCO NPs grafted onto them. However, due to the resonant nature of the excitation, SCO-induced NLO switching was not observed.

The 1 : 1 : 1 reaction of YbCl3·6H2O, K3[Co(CN)6] and bpyO2 in H2O has provided access to a complex with formula [YbCo(CN)6(bpyO2)2(H2O)3]·4H2O (1) in a very good yield while its structure has been determined by single-crystal X-ray crystallography and characterised based on elemental analyses and IR spectra. Magnetic susceptibility studies showed the complex to be a field induced single molecule magnet, as confirmed by μ-SQUID measurements. CASSCF calculations confirm the existence of a mJ = 7/2 ground state, with rather large transverse components, responsible for the fast relaxation characteristic of compound 1 at zero DC field, which is reduced upon application of DC fields. Moreover, a combination of luminescence studies along with CASSCF calculation allows the identification of the band structure of the complex, which is ultimately related to its electronic properties. Compound 1 operates as a luminescent thermometer in the 125-300 K range with a maximum relative thermal sensitivity of ≈0.1% K-1 at 180 K.

Two three-dimensional (3-D) polycyanidometallate-based luminescent thermometers with the general formula {Ln4Co4(CN)24(4-benpyo)17(H2O)·7H2O}n Ln = (Dy(III)(1), Eu(III)(2)), based on the red-emissive diamagnetic linker [Co(CN)6]3- and the bulky pyridine derivative that possesses the N-oxide moiety, 4-benzyloxy-pyridine N-oxide (benpyo), were prepared for the first time. The structure of compound 1 has been determined by single-crystal X-ray crystallography while the purity and structure of 2 have been confirmed by CHN, Fourier transform infrared spectroscopy (FT-IR), and powder X-ray diffraction (PXRD) analysis. Magnetic AC susceptibility measurements at zero field show no single-molecule magnet (SMM) behavior indicating fast relaxation operating in 1. Upon application of an optimal field of 2 kOe, the SMM character of compound 1 is revealed while the τ(Τ) can be reproduced solely considering the Raman process τ-1 = CTn with C = 7.0901(3) s-1 K-n and n = 3.58(1), indicating that a high density of low-lying states and optical as well as acoustic phonons play a major role in the relaxation mechanism. Micron-sized superconducting quantum interference device (μ-SQUID) loops show a very narrow opening in agreement with the AC susceptibility studies and complete active space self-consistent field (CASSCF) calculations. The interaction operating between the Dy(III) ions was quantified from CASSCF calculations. Good agreement is found by fitting the experimental DC χMΤ(Τ) and M(H), employing the Lines model, with JLines = -0.087 cm-1 (-0.125 K). The excitation spectra of compound 2 are used for temperature sensing in the 25-325 nm range with a maximum relative thermal sensitivity, Sr = 0.6% K-1 at 325 K, whereas compound 1 operates as a luminescent thermometer based on its emission features in the temperature range of 16-350 K with Sr ≈ 2.3% K-1 at 240 K.

The 1:1:1 reaction of DyCl3·6H2O, K3[Co(CN)6] and bpyO2 in H2O has provided access to a complex with formula [DyCo(CN)6(bpyO2)2(H2O)3]·4H2O (1) in a very good yield, while [DyFe(CN)6(bpyO2)2 (H2O)3]·4H2O (2) was also precipitated (also in a high yield) using K3[Fe(CN)6] instead of K3[Co(CN)6]. Their structures have been determined by single-crystal X-ray crystallography and characterized based on elemental analyses and IR spectra. Combined direct current (dc) and alternating current (ac) magnetic susceptibility revealed slow magnetic relaxation upon application of a dc field. μ-SQUID measurements and CASSCF calculations revealed high-temperature relaxation dynamics for both compounds. Low-temperature magnetic studies show the relaxation characteristics for 1, while for compound 2 the dynamics corresponds to an antiferromagnetically coupled Dy···Fe pair. High-resolution optical studies have been carried out to investigate the performance of compounds 1 and 2 as luminescence thermometers. For 1, a maximum thermal sensitivity of 1.84% K-1 at 70 K has been calculated, which is higher than the acceptable sensitivity boundary of 1% K-1 for high-performance luminescence thermometers in a broad range of temperature between 40 and 140 K. Further optical studies focused on the chromaticity diagram of compound 1 revealed a temperature shift from warm white (3200 K) at 10 K toward a more natural white color near 4000 K at room temperature.

Coordination polymers (CPs) with a dual emission spanning from the visible (vis) to near-infrared (NIR) regions of the electromagnetic spectrum are used for optical sensors, medical diagnostics, and telecommunication technologies. We herein report the synthesis, structural characterization, and optical response of heterometallic cyanido-bridged layered {[EuxNdy(4-OHpy)2(H2O)3][Co(CN)6]} CPs, where 4-OHpy = 4-hydroxypyridine, with a multicolor emission profile across the vis and NIR regions. The crystals show an efficient energy transfer (ET) from the 4-OHpy ligand and the [Co(CN)6] ions to the Eu3+ and Nd3+ ions, resulting in an enhanced photoluminescence (PL) efficiency. We study the ET with steady-state and time-resolved PL, reporting an ET between the Ln3+ centers. The excitation-dependent emission of the mixed Ln3+ CPs and the control over the PL lifetime yield new insights into the optoelectronic properties of these materials.

The 1 : 2 reaction between Dy(O2CMe)3·4H2O and 1-acetyl-2-napthol (LH) in MeOH has provided access to the complex [Dy2L6(MeOH)]·MeOH (1·MeOH) in a good yield. The structures of the isomorphous complex 1·MeOH and its doped diamagnetic yttrium analogue [Dy0.14Y1.86L6(MeOH)]·MeOH (Dy@Y2) have been determined by single-crystal X-ray crystallography and characterized based on elemental analyses, IR spectra, and powder X-ray patterns. Combined dc and ac magnetic susceptibility and the magnetization data for 1 suggest that this complex shows slow magnetic relaxation. Under a 0 Oe dc field, a single relaxation mechanism is seen while two magnetization relaxation processes are evident under a 1500 G external magnetic field. The fit to the Arrhenius law has been performed using the 1.8-10 K ac data, affording an effective barrier for the magnetization reversal of 13 K and 7 K under the external dc field. Theoretical studies have been performed using ab initio and density functional methodologies to understand the electronic structure and the magnetic relaxation dynamics resulting from the single DyIII ion as well as from the dinuclear exchange-coupled states. Rich powder EPR spectra at the X-band and Q-band were obtained from Dy@Y2, as well as from the 1·MeOH dimer, while simulation studies revealed the ferromagnetic nature of the interaction between the DyIII ions in accordance with theoretical studies.

Aminated silica hybrid, spin-crossover (SCO) nanoparticles (AmNPs) coupled with (S)-naproxen (NAP) were proposed for potential drug nanocarriers through drug release experiments at various pH values. DNA- and albumin-binding studies were also carried out using diverse techniques in order to investigate the interaction of the nanoparticles with calf-thymus DNA and serum albumins and to determine the corresponding binding constants.

The extreme downsizing effect on 2D SCO nanoparticles resulted in a two-step hysteretic behavior and stability in aqueous dispersions.

A reverse micelle method was used for the synthesis of water-soluble silica hybrid, spin-crossover (SCO) nanoparticles (NPs). MRI experiments provided temperature dependent T2 values, indicating their potential use as smart MRI agents, while lyophilization of NP dispersions in water yielded powders with a preserved but modified thermal hysteretic magnetic profile.

Spin Crossover (SCO) particles at the nanometric scale provide an alternative point of view and a new perspective concerning the development of a new generation of spintronic, electronic, photonic and mechanical devices. The coexistence of the SCO phenomenon with the accompanying hysteresis loop enhances the functionality of future devices for storing and processing information. Despite all promising facts, the SCO phenomena are greatly affected by cooperativity issues resulting in a direct relation between the decrease of the size of nanopatricle and the overall decrease of cooperativity towards more gradual spin transitions. This minireview aims to summarise the synthetic techniques for the synthesis of 2-D FeII SCO particles at the nanometric scale, an underexplored area of research, highlighting the effects of the size-reduction on the magnetic properties of the corresponding nanoparticles and hopefuly showcasing the importance of studying in the context of 2D limit the SCO phenomena.