Curing behaviour of DGEBA was investigated in the presence of varying molar ratio of biuret and 4,4′-diaminodiphenylsulfone (DDS) by means of Differential scanning calorimetery. The multiple heating rate method (5, 10, 15 and 20 °C min−1) was used to study the curing behaviour of epoxy resins. The peak exotherm temperature was found to be dependent on the heating rates, structure of biuret as well as on the ratios of biuret:DDS used. Ozawa method was used for calculating the activation energy of curing reaction. The thermal stability of the isothermally cured resins was evaluated by recording the thermogravimetric traces in nitrogen atmosphere. All the samples were stable up to 330 °C.

Curing kinetics of diglycidyl ether of bisphenol-A (DGEBA) in the presence of varying molar ratios of derivatives of stannanes to 4,4'-diaminodiphenylsulfone (DDS) was investigated by the dynamic differential scanning calorimetry. The derivatives were synthesized by reacting 1 mole of biguanide (B) with 1 mole of phenylethyltindihydride (PETH) or phenylmethyltindihydride (PMTH) or phenylbutyltindihydride (PBTH) and designated as BPETH or BPMTH or BPBTH respectively. These derivatives were characterized by elemental analysis and spectroscopic techniques such as IR, (1)H NMR, (13)C NMR and (119)Sn NMR. The mixtures of these derivatives to DDS at ratios of 0 : 1, 0.25 : 0.75, 0.5 : 0.5, 0.75 : 0.25 and 1 : 0 were used to investigate the curing behaviour of DGEBA. The multiple heating rate method (5, 10, and 15 and 20 degrees C.min(-1)) was used to study the curing kinetics of epoxy resins. The thermal stability of the isothermally cured resins was also evaluated using dynamic thermogravimetry in a nitrogen atmosphere.