As the traffic volume and wheel load on the orthotropic deck of a long-span steel bridge increase, longitudinal cracks often develop in the asphalt concrete surfacing leading to deterioration. The purpose of this study was accordingly to derive the fatigue failure evolution law of this surfacing. The fatigue damage evolution mechanism was studied from a micro perspective to derive a general fatigue damage evolution law. Fatigue tests and theoretical predictions of fatigue life were then performed for different asphalt concrete surfacing types commonly used in the decks of long-span steel bridges to verify the derived law.

The crack initiation and life prediction of fiber-reinforced asphalt concrete (FRAC) surfacing for steel bridge decks under a cyclic vehicle load are analyzed from the perspective of damage mechanics. The damage field and the stress and strain field evolution rule of a composite beam in fatigue test are studied, and a fatigue failure criterion is proposed for steel deck FRAC surfacing. Bending fatigue tests are performed on composite beams composed of a steel deck and polyacrylonitrile (PAN)-fiber-reinforced Gussasphalt (GA), i.e., GA-PAN, concrete surfacing under different fiber content and temperature conditions. The damage evolution characteristics of GA-PAN concrete surfacing over the steel deck with different fiber lengths and volume ratios are predicted by analyzing the fatigue life equations. The results show that the steel bridge deck FRAC surfacing model can reflect the comprehensive influence of the fiber content and length on the fatigue performance of steel bridge AC. Specifically, a lower temperature results in the fiber more synergistically affecting the fatigue resistance of AC. Theoretically, the service performance of asphalt concrete increases with the increase of fiber length and content. The optimum fiber length and volume ratio of GA-PAN are found to be 9 mm and 0.46–0.48%, respectively, considering the construction workability.

针对钢桥面铺装工程中普遍采用的改性沥青(Stone Matrix Asphalt,SMA)、浇筑式沥青(Guss asphalt,GA)、环氧沥青(Epoxy asphalt,EP)混合料双层铺装结构,进行了循环车载作用下钢桥面与沥青混凝土铺装疲劳损伤特性理论分析与试验研究.基于疲劳损伤度,研究了钢桥面铺装疲劳损伤失效行为和疲劳开裂过程中损伤场、应力和应变场动态演变机制,推导出疲劳失效时的损伤场、应力和应变场计算表达式,并给出钢桥面铺装疲劳寿命理论公式.以三座钢箱梁桥桥面铺装(润扬长江大桥2005,南京长江三桥2005,苏通大桥2008)为例,对不同铺装结构组合方案下的复合梁进行疲劳试验分析和使用寿命理论预测.实例研究结果表明,钢桥面铺装疲劳损伤失效行为预估模型合理可行;相较于改性沥青、浇筑式沥青,环氧沥青混合料具有较强高的强度低变形能力,更适合于大跨径钢桥面铺装抗疲劳的设计要求;由环氧沥青混合料组合而成的“双层环氧沥青混凝土”和“浇注式沥青混凝土(下层)+环氧沥青混凝土(上层)”的抗疲劳性能优于其它沥青混合料铺装结构组合方案,同等厚度组合情况下疲劳使用寿命可延长1倍～2倍以上;“双层环氧沥青混凝土”已应用于润扬长江大桥、南京长江三桥和苏通长江大桥钢桥面工程,并已成功运行10年以上,其跟踪观测结果良好.

Epoxy asphalt (EA) concrete is widely used in constructing long-span steel bridge pavements (SBDPs). This study aims to derive a fatigue damage evolution law, conducting an experimental investigation of SBDP. First, a general theoretical form of the fatigue damage evolution law of materials is established based on the thermal motion of atoms. Then, fatigue experiments demonstrate that this evolution law well represents the known damage–life relationships of SBDP. Taking into account the experimental relationships between damage and fatigue life under symmetrical cyclic loadings with different overload amplitudes and temperature variations, a detailed damage evolution law is deduced. Finally, the role of damage accumulation is discussed on the basis of the proposed damage evolution law for the extreme situation of heavy overload and severe environments. The results show that both heavy loading and falling temperatures increase the fatigue damage of SBDP considerably; therefore, SBDP should avoid heavy loading combined with winter temperatures. EA shows a fatigue life two to three times longer than that of modified matrix asphalt (SMA) or guss asphalt (GA). For the same thickness, EA pavement is demonstrated to be more suitable for an anti-fatigue design of large-span SBDP under high traffic flows and low temperatures.

Epoxy asphalt (EA) concrete is widely used in constructing long-span steel bridge pavements (SBDPs). This study aims to derive a fatigue damage evolution law, conducting an experimental investigation of SBDP. First, a general theoretical form of the fatigue damage evolution law of materials is established based on the thermal motion of atoms. Then, fatigue experiments demonstrate that this evolution law well represents the known damage-life relationships of SBDP. Taking into account the experimental relationships between damage and fatigue life under symmetrical cyclic loadings with different overload amplitudes and temperature variations, a detailed damage evolution law is deduced. Finally, the role of damage accumulation is discussed on the basis of the proposed damage evolution law for the extreme situation of heavy overload and severe environments. The results show that both heavy loading and falling temperatures increase the fatigue damage of SBDP considerably. EA shows a fatigue life two to three times longer than that of modified matrix asphalt (SMA) or guss asphalt (GA). For the same thickness, EA pavement is demonstrated to be more suitable for an anti-fatigue design of large-span SBDP under high traffic flows and low temperatures.