Safety-relevant components, for which a failure in service could have catastrophic consequences, are usually designed for extremely low probability of failure and they are subjected to stringent part qualification procedures according to guidelines set by regulatory agencies. Manufacturers are often forced to perform tests on full scale or scaled components to ensure the structural integrity under defined loading conditions, which usually implies a huge experimental and financial effort. Therefore, companies try to develop new strategies such as digital twins, which allow to massively reduce costs, without compromising safety. This work presents a new quasi-static testing and assessment concept, the main idea of which is to replace, or at least reduce, the experimental testing on components by testing specimens representative of the component.Fracture mechanics specimens have been designed iteratively by numerical simulations to match the stress state at the crack-tip of the maximum permissible defect defined by regulatory agencies for the component. Potentially, the major benefit of the proposed approach is that the tests can be performed on conventional laboratory testing machines. The effectiveness of the methodology is demonstrated in case of the structural integrity assessment of a Ni-base superalloy aero-engine turbine disk at overspeed conditions.

Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present two alternative burst speed assessment methods under development based on the Failure Assessment Diagram (FAD) and a global stability criterion, respectively. In the scope of the fracture mechanics assessment, the failure modes hoop-burst and rim-peeling are investigated with semi-circular surface cracks modelled at the critical regions on the turbine disk. The comparison of the predicted critical rotational speed shows good agreement between the assessment methods.

In 2015, the University of Manchester hosted a workshop ('Mind the Gap') aimed at identifying gaps in a number of structural integrity fitness-for-service procedures, including R5, R6, BS 7910 and API/ASME. The findings were subsequently summarised in a journal paper and shared with the relevant stakeholders. A second workshop, this time hosted by the University of Bristol in 2017, was intended to build on the findings of the earlier event, identifying which gaps had been filled, which remain and whether new ones have been identified in the meantime. 'Mind the Gap 2' was wide-ranging, including consideration of failure by fracture, fatigue crack growth, hightemperature creep and environmentally assisted crack growth, along with the use of innovative techniques to follow the progress of crack growth from the atomic to the macroscopic scale. A summary of the whole event is thus outside the scope of a single paper, so here we concentrate mainly on advances in fracture assessment, on the interface between inspection and ECA, and on how developments are being incorporated into structural integrity procedures. There is a particular emphasis on the energy transition in the UK, where the planned energy mix will include both nuclear power and offshore wind.

Using the case study of a fail-safe design criterion for a steering knuckle of a commercial vehicle, the effect of stiffness/constraint on the crack driving force in the component is discussed. The problem arises when assessment procedures such as R6, BS 7910 or SINTAP/FITNET are applied in conjunction with substitute geometries for determining the model parameters K-factor and limit load (or a substitute for the latter), as it is common practice. In the example, the conservatism was so pronounced that this procedure was in fact unusable. A way out could be the finite element-based determination of the model parameters and their use in the analytical framework. This procedure is useful and effective if the finite element-based calculations are used in parameter sensitivity analyses.

Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. In particular, the rim-peeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk, with the crack plane perpendicular to the radial direction. The crack is therefore subjected to a biaxial stress state and grows under increasing rotational speed until it triggers the rim-peeling failure. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of J-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest J-integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. Probabilistic aspects are also considered in the calculations.

The threshold against fatigue crack propagation (ΔKth) is a crucial parameter for the damage tolerance assessment of engineering components subjected to cyclic loading and it is composed by two distinct components, one intrinsic, dependent on the elastic material properties and the lattice type, and one extrinsic, related to the occurrence of crack closure effects. An important issue is that several factors can influence ΔKth and, in general, the fatigue crack propagation behavior. In this work, the influence of the experimental procedure, air humidity, stress ratio and test frequency on da/dN-ΔK data has been investigated. Results are discussed with their potential causes and consequences on the calculations of the residual lifetime.

Abstract Der Aufsatz gibt eine Übersicht über die wichtigsten bruchmechanischen Fragestellungen bei Eisenbahnkomponenten sowie vorhandene Lösungsansätze. Schwerpunktmäßig orientiert er sich an den sicherheitsrelevanten Komponenten Radsatzwelle, Rad und Schiene. Die verschiedenen in der Praxis beobachteten Schädigungsformen an Eisenbahnkomponenten werden hinsichtlich ihrer möglichen Einbindung in ein bruchmechanisches Bewertungskonzept diskutiert.

Additive manufacturing (AM) is becoming increasingly important in engineering applications due to the possibility of producing components with a high geometrical complexity allowing for optimized forms with respect to the in-service functionality. Despite the promising potential, AM components are still far from being used in safety-relevant applications, mainly due to a lack of understanding of the feedstock-process-properties-performance relationship. This work aims at providing a full characterization of the fatigue behavior of the additively manufactured AISI 316L austenitic stainless steel and a direct comparison with the fatigue performance of the wrought steel. To this purpose, a set of specimens has been produced by laser powder bed fusion (L-PBF) and subsequently heat treated at 900 °C for 1 hour for complete stress relief, whereas a second set of specimens has been machined out of hot-rolled plates. Low cycle fatigue (LCF) and high cycle fatigue (HCF) tests have been conducted for characterizing the fatigue behavior. The L-PBF material had a higher fatigue limit and better finite life performance compared to wrought material. Both, LCF and HCF-testing revealed an extensive cyclic softening.

In the framework of the fatigue assessment of welded components, several methods are available in design standards such as the nominal stress, hot-spot stress, notch stress and linear elastic fracture mechanics approaches. The present paper aims at comparing two advanced local approaches for the fatigue strength assessment of different welded joints made of steel. The first one is IBESS which is based on short crack fracture mechanics. The second one is the PSM which instead involves the strain energy density approach. Both methods will be briefly presented, and the fatigue life prediction results discussed. The results obtained for the joint geometries considered in this work show advantages and drawbacks of the approaches, which are thoroughly analysed as well.

The Kitagawa-Takahashi (KT) diagram is a proven concept for describing the fatigue limit in presence of a defect or crack. It can be determined empirically with great experimental effort. It can also be estimated by means of the El Haddad relationship if the endurance limit and the long fatigue crack propagation threshold are available in reasonable accuracy. A third option is the determination using the cyclic R-curve, which describes the dependency of the fatigue crack propagation threshold on the crack growth at the short crack propagation stage. This can be experimentally determined using a closure-free initial pre-crack. It can then be applied to the determination of crack arrest for a given applied load and a given defect or crack size. Compared to the other two methods mentioned above, this option has considerable advantages: It can be applied to any component and any stress ratio. It allows the treatment of multiple cracks and provides estimations of the S-N curve in the finite life regime as well as at the endurance limit. Compared to the empirical determination of the KT diagram, the experimental effort is significantly lower and compared to the El Haddad approach it avoids problems such as the use of non-conservative long fatigue crack propagation thresholds (when the conventional load reduction method is applied to materials prone to corrosion) and the mathematical predetermination of the curve shape. The work introduces the method and provides a critical discussion as well as quantitative comparison between the different methods.

The impact of crack closure and environmental effects on the experimental determination of the fatigue crack propagation threshold is a major problem for the assessment of cyclically loaded components, especially low stress ratios . In this work, the influence of the experimental procedure and air humidity on d/d data at different is discussed. Unlike the results at = -1, the threshold values obtained at & AP; 0.8, i.e. under negligible crack closure levels, show a very small scatter band regardless of the variation of the test parameters and environmental conditions.

The robust determination of the threshold against fatigue crack propagation ΔKth is of paramount importance in fracture mechanics based fatigue assessment procedures. The standards ASTM E647 and ISO 12108 introduce operational definitions of ΔKth based on the crack propagation rate da/dN and suggest linear fits of logarithmic ΔK– da/dN test data to calculate ΔKth. Since these fits typically suffer from a poor representation of the actual curvature of the crack propagation curve, a method for evaluating ΔKth using a nonlinear function is proposed. It is shown that the proposed method reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density.

If a component is cyclically loaded, the load carrying capacity is considerably lower than in the monotonic case. This general observation applies in particular to L-PBF parts. The causes of this are mainly material defects such as pores and lack of fusion (Chapter 6) and a pronounced surface roughness in the as-built condition (Chapter 7). In addition, effects due to the anisotropy of the microstructure (Chapter 8) and a complex residual stress pattern (Chapter 9) play an important role. A consequence is that common strategies for fatigue assessment cannot be transferred to L-PBF applications without modifications. Due to the inhomogeneity of the material, the determination of representative material properties and the transfer to the component is a problem, and this is also the case with regard to the consideration of defects, surface roughness, and residual stresses. The chapter gives a brief introduction to these problem areas.

The safe fatigue design of metallic components fabricated by additive manufacturing (AM) is still a largely unsolved problem. This is primarily due to (a) a significant inhomogeneity of the material properties across the component; (b) defects such as porosity and lack of fusion as well as pronounced surface roughness of the as-built components; and (c) residual stresses, which are very often present in the as-built parts and need to be removed by post-fabrication treatments. Such morphological and microstructural features are very different than in conventionally manufactured parts and play a much bigger role in determining the fatigue life. The above problems require specific solutions with respect to the identification of the critical (failure) sites in AM fabricated components. Moreover, the generation of representative test specimens characterized by similar temperature cycles needs to be guaranteed if one wants to reproducibly identify the critical sites and establish fatigue assessment methods taking into account the effect of defects on crack initiation and early propagation. The latter requires fracture mechanics-based approaches which, unlike common methodologies, cover the specific characteristics of so-called short fatigue cracks. This paper provides a discussion of all these aspects with special focus on components manufactured by laser powder bed fusion (L-PBF). It shows how to adapt existing solutions, identifies fields where there are still gaps, and discusses proposals for potential improvement of the damage tolerance design of L-PBF components.

This paper presents the application of short crack propagation models based on the cyclic R-curve for assessing the fatigue strength of additively manufactured (AM) materials containing fabrication defects. Chapetti’s and IBESS models were implemented in combination with Murakami’s area parameter, considering recently published data on laser powder bed fusion processed AISI 316L stainless steels. Estimated S-N curves and Kitagawa-Takahashi diagrams predict fairly well the experimental data, especially the origin of the failure from internal or surface defects. These results provide an indication that the methods based on the cyclic R-curve constitute suitable tools for fatigue behavior assessment of AM materials.