Synergistic Removal of Humic Acid in Water by Coupling Adsorption and Photocatalytic Degradation Using TiO2/Coconut Shell Powder Composite

The feasibility of applying nanoscale TiO2/coconut shell powder TCNSP composite to remove HA in aqueous solution was evaluated, and the optimization of the photocatalytic systems using newly developed TCNSP composite was performed. The developed TCNSP composite has high specific surface area i.e., 454 m2/g and great porosity i.e., 66.9% with pore size of less than 5 μm. High removal efficiencies ≥95% of HA were observed due to the significant synergistic effects by coupling adsorption and photocatalytic reaction of TCNSP composite. As the initial concentration of HA increased, the degradation rate Kapp decreased due to HA sorption saturation to the surface of TCNSP composite and the photon interception by HA molecules in aqueous solution. Since the increased loading amount of TCNSP composite enhanced the number of active sites, Kapp values increased until the optimum loading amount of TCNSP composite. As pH values increased, HA removal efficiency decreased due to increasing electrostatic repulsion between HA and TCNSP composite. Based on the response surface methodology, higher HA removal efficiencies were obtained with acidic condition, longer reaction time, and appropriated loading amount of TCNSP. Further pilot-scale study is in progress using TCNSP composite combined with UVC to remove HA from large amounts of surface water i.e., 200 m3/d.