Innovation and entrepreneurship are based on new combinations, constructed within social networks. The literature on social networks refers to Schumpeter's analysis of new combinations, but is limited in its use of his understanding of the range of innovations and long-term aspects of entrepreneurship. Using the case of Josiah Wedgwood, a quintessential Schumpeterian entrepreneur, this article analyses how social networks contribute to a broad range of innovations over an extended period, involving both strong and weak ties. It shows how social network research in innovation and entrepreneurship benefits from Schumpeterian insights on the wide forms of innovation and longer term influences on network structures.
以分析纯的硝酸铝和碳酸氢铵为主要原料,采用共沉淀法制备纳米氧化铝粉体,研究反应物的加料顺序和加料速度、表面活性剂种类、溶剂组成、晶种及前驱体的煅烧温度对产物的影响.采用X射线衍射仪分析粉体的物相组成,用谢乐公式计算晶粒尺寸,采用透射电子显微镜观测颗粒形貌.结果表明:原料的加料顺序对产物影响不明显,用PEG6000作表面活性剂,水和乙醇等体积混合液作溶剂,Al(NO3)3溶液直接倒入NH4HCO3溶液中制得前驱体,当煅烧温度为1135 ℃煅烧2 h时,制备了粒径为33 nm的α-Al2O3粉体,加入晶种后,煅烧温度可降低至1075 ℃.
采用溶胶—凝胶和固相反应相结合的方法制备了 ZnO/BiFeO3复合陶瓷,并对陶瓷样品进行了物相结构、微观形貌和电学性能的研究.研究表明:纳米粉体的退火温度为550 ℃、复合陶瓷煅烧温度为800 ℃、纳米ZnO添加量为7.5％时,所制复合陶瓷的晶粒形状和尺寸较为规则,Pr、Ps和Ec分别为0.053 µC.cm·2、0.388 μC·cm-2和5.58 kV·cm-1.
1600 ℃常压烧结制备了氧化锆增韧氧化铝(ZTA)陶瓷,研究添加Cr2O3在ZTA陶瓷中的呈色性能是否优异.结果表明:适量的Cr2O3加入ZTA陶瓷中会固溶进Al2O3,烧结后样品均呈现出粉红色,并且随着Cr2O3添加量的增大,样品对可见光(400-700nm)的反射率逐渐下降,即粉色不断加深,样品颜色的明度值不断下降,饱和度不断上升,a*值始终大于零且数值不断增大,也说明样品的粉色不断加深.测试其力学性能发现:当Cr2O3添加后,小幅提高样品的力学性能,在添加量为0.7wt.％左右时,达到最大值;但添加量超过0.7wt.％时,样品的力学性能和致密度有小幅下降,原因可能是过量的Cr2O3加入后,导致了样品内部气孔增多.
采用动态热机械分析法(DMA)研究了国产KD-SA型碳化硅(SiC)纤维单丝的力学性能.试验对KD-SA型SiC纤维分别进行了 1200 ℃、1300 ℃、1400 ℃和1500 ℃空气环境下的热处理,采用DMA的频率扫描模式测定了未处理和处理后的试样储能模量和损耗角正切.此外,试样的强度也同时使用小载荷万能试验机进行测定.试验发现:经过高温处理的样品,其拉伸强度迅速降低至未处理样品强度的1/2左右.同时,高温处理后,试样的储能模量也远低于未处理试样.高温处理的SiC纤维的力学性能迅速降低,主要归结于高温下的氧化机制.因此,对高温处理样品的截面和表面进行了扫描电镜观察,发现了在高温下,晶粒变大、产生松散结构的现象.最后,高温处理和未经处理样品的储能模量和损耗对频率的依赖性通过DMA试验,并进行了验证和讨论.