The Murmansk region has a significant amount of sulfide copper-nickel raw materials. Deposits of the Nud massif associated with Monchepluton are promising for processing. The Nud II deposit cut-off grade ore with an initial Ni content of 0.45 % and Cu of 0.39 % has been chosen as the research object. During the research, the ore was mixed with ammonium sulfate, grinded, and the mixture was roasted in a muffle furnace with static air atmosphere. The roasted mixture was leached in heated distilled water with constant stirring. The maximum metals recovery was achieved when crushing to a fraction of –40 µm, the ratio of ore : ammonium sulfate is equal to 1 : 7, roasting temperature 400 °C, roasting duration 300 min. In the mixture roasted at these parameters, reflexes of copper and nickel sulfates were recorded by the x-ray phase analysis (XRD) method. At the stage of water leaching, the maximum recovery was: Ni – 79.1 %, Cu – 75.8 %.

Nanocrystalline ytterbium zirconate Yb4Zr3O12 (δ-phase) was synthesized by the solid-state method with preliminary mechanical activation of a stoichiometric mixture of the corresponding oxides. The processes occurring in the course of the synthesis were studied by X-ray powder diffraction, IR spectroscopy, and thermal analysis. The average size of Yb4Zr3O12 crystallites obtained by annealing a mechanically activated oxide mixture at 900, 1000, 1100, and 1200°C was calculated by the Scherrer formula and was 12, 17, 27, and 41 nm, respectively.

Multi-stage deposition of metals from a sulfate solution with a high concentration of iron, aluminum, copper, zinc, and nickel has been studied. The concentrations of the components correspond to the composition of the sub-basement waters of the Gaisky GOK. Granular magnesia-silicate reagent based on serpentinite (Khalilovsk magnesite deposit, the Orenburg region, Russia) has been used as an alkaline agent. The magnesia-silicate reagent's ability to reduce the acidity of solutions is due to the presence of products of destruction of the original serpentine mineral, mainly magnesium oxide. The results of the solutions multi-stage purification from metals simulation have been presented. It has been found that the reagent did not wholly exhaust its activity during a single contact with the solution. Therefore, the possibility of its repeated use for the 2nd and 3rd time has been studied. As the solution is neutralized according to the known pH range of the beginning and complete deposition of metal compounds, first iron, and then aluminum are deposited. For copper and nickel, the effect of co-precipitation is observed until the pH of precipitation of poorly soluble compounds is reached. Iron is the main component of precipitations at the 1st, 2nd, and 3rd stages, which corresponds to pH = 2.4-3.7. At the 4th stage (pH = 4.0), the precipitations consisted mainly of aluminum compounds. The copper and nickel content in precipitations increase due to decreased concentration of major components (aluminum and iron) and a pH increase. The deposition of zinc from the solution occurs not to the precipitations, but on the granules surfaces. Precipitations enriched in aluminum and iron have been obtained. Sorption and co-precipitation processes have been observed for copper, zinc, and nickel, which prevents individual precipitation by these metals. Thermally activated serpentine minerals can be considered a promising alkaline reagent for technogenic solutions neutralization and purification.

Синтез геополимеров на основе золы уноса с применением механоактивацииКалинкин А.М., Гуревич Б