The members of the CuMo(1- x)WxO4 series (0 < or = x < 0.1) undergo a first-order phase transition that can be induced by pressure application; the thermochromic properties of such a series have already been reported. The two polymorphic forms exhibit two distinguishable colors: green for the low pressure form (alpha) and brownish-red for the high pressure one (gamma). These oxides can open up a new market for friendly pressure indicators, particularly for the compositions (0.07 < or = x < or = 0.1) for which the two polymorphs are stable at room temperature, that is, for which the color transition via pressure application is nonreversible. Within the CuMo(1- x)WxO4 solid solution domain, the dependence of the transition pressure versus tungsten content, temperature of measurement, and sample thermal-pressure history was studied. A large control of the transition pressure (from 5 to several 100 MPa) was brought to the fore. The transition was then studied using X-ray diffraction and transmission electron microscopy-energy dispersive X-ray analyses. This first-order transition, occurring by atomic migration inside the cell, seems to be preceded by an atomic disordering; moreover, transition temperatures may be modified by W segregation at the surface of the grains.

A drastic color transition from green to brownish-red in the CuMo1-xWxO4 system occurs during a first-order phase transition. This study shows that it is possible to control this transition in terms of temperature or pressure with respect to the tungsten content (see figure). Hence, the use of these compounds for new applications as temperature indicators or shock detectors is feasible.

The members of the CuMo1-xWxO4 series (0alpha transition can occur between 260 and 360 K, and the alpha-->gamma transition between 175 and 275 K as a function of x. The control of the alpha/gamma transition temperatures with x is related to the larger propensity of tungsten compared to molybdenum, to adopt a tetrahedral environment.