In this paper, we report on the results of the study of the Ti/Au/n-GaAs planar Schottky diodes (PSD) intended for the wideband detection of terahertz radiation. The two types of the PSD devices were compared having either the dual n/n(+) silicon dopant profile or the triple one with a moderately doped matching sublayer inserted. All the diodes demonstrated no noticeable temperature dependence of ideality factors and barrier heights, whose values covered the ranges of 1.15-1.50 and 0.75-0.85 eV, respectively. We observed the lowering of the flat band barrier height of similar to 80 meV after introducing the matching sublayer into the GaAs sandwich. For both the devices types, the series resistance value as low as 20 Omega was obtained. To extract the total parasitic capacitance, we performed the Y-parameters analysis within the electromagnetic modeling of the PSD's behavior via the finite-element method. The capacitance values of 12-12.2 fF were obtained and further verified by measuring the diodes' response voltages in the frequency range of 400-480 GHz. We also calculated the AC current density distribution within the layered structures similar to those being experimentally studied. It was demonstrated that insertion of the moderately Si-doped matching sublayer might be beneficial for implementation of a PSD intended for the operation within the 'super-THz' frequency range.

Superconducting single-photon detector (SSPD) is a planar nanostructure patterned from 4-nm-thick NbN film deposited on sapphire substrate. The sensitive element of the SSPD is 100-nm-wide NbN strip. The device is operated at liquid helium temperature. Absorption of a photon leads to a local suppression of superconductivity producing subnanosecond-long voltage pulse. In infrared (at 1550 nm and longer wavelengths) SSPD outperforms avalanche photodiodes in terms of detection efficiency (DE), dark counts rate, maximum counting rate and timing jitter. Efficient single-mode fibre coupling of the SSPD enabled its usage in many applications ranging from single-photon sources research to quantum cryptography. Recently we managed to improve the SSPD performance and measured 25% detection efficiency at 1550 nm wavelength and dark counts rate of 10 s-1. We also improved photon-number resolving SSPD (PNR-SSPD) which realizes a spatial multiplexing of incident photons enabling resolving of up to 4 simultaneously absorbed photons. Another improvement is the increase of the photon absorption using a λ/4 microcavity integrated with the SSPD. And finally in our strive to increase the DE at longer wavelengths we fabricated SSPD with the strip almost twice narrower compared to the standard 100 nm and demonstrated that in middle infrared (about 3 μm wavelength) these devices have DE several times higher compared to the traditional SSPDs.