All-dielectric gratings are ideal for high average power laser pulse compressors due to their low loss and high diffraction efficiencies. However, they have not been utilized in petawatt-class lasers with pulse durations below 100 fs due to a variety of challenges. We present a resonance-free design for low-dispersion (1480 lines/mm) diffraction gratings made of dielectric materials resistant to femtosecond laser damage (SiO2/HfO2). A 14 cm diameter sample was fabricated resulting in a mean diffraction efficiency of 99.1% at lambda = 810 nm with high spatial uniformity using equipment which can produce gratings up to 1 m diagonal. The implementation of these gratings in the compression of 30 fs pulses in an out-of-plane geometry can result in compressor efficiencies approaching 95%. The measured laser absorption is 500 x lower than current ultrafast petawatt-class compressor gratings enabling a substantial increase in average power handling capabilities of these laser systems.

We have developed a high-efficiency (~90%), broad-bandwidth low-absorption pulse compressor suitable for high energy pulses. This technology is a significant step in enabling high peak power laser systems to operate at high repetition rates.

Laser energy absorption and subsequent heat removal from diffraction gratings in chirped pulse compressors poses a significant challenge in high repetition rate, high peak power laser development. In order to understand the average power limitations, we have modeled the time-resolved thermo-mechanical properties of current and advanced diffraction gratings. We have also developed and demonstrated a technique of actively cooling Petawatt scale, gold compressor gratings to operate at 600W of average power - a 15x increase over the highest average power petawatt laser currently in operation. Combining this technique with low absorption multilayer dielectric gratings developed in our group would enable pulse compressors for petawatt peak power lasers operating at average powers well above 40kW.

We investigate the laser damage resistance of multilayer dielectric (MLD) diffraction gratings used in the pulse compressors for high energy, high peak power laser systems such as the Advanced Radiographic Capability (ARC) Petawatt laser on the National Ignition Facility (NIF). Our study includes measurements of damage threshold and damage density (ρ(Φ)) with picosecond laser pulses at 1053 nm under relevant operational conditions. Initial results indicate that sparse defects present on the optic surface from the manufacturing processes are responsible for damage initiation at laser fluences below the damage threshold indicated by the standard R-on-1 test methods, as is the case for laser damage with nanosecond pulse durations. As such, this study supports the development of damage density measurements for more accurate predictions on the damage performance of large area optics.

Precise assessment of the high fluence performance of pulse compressor gratings is necessary to determine the safe operational limits of short-pulse high energy lasers. We have measured the picosecond laser damage behavior of multilayer dielectric (MLD) diffraction gratings used in the compression of chirped pulses on the Advanced Radiographic Capability (ARC) kilojoule petawatt laser system at the Lawrence Livermore National Laboratory (LLNL). We present optical damage density measurements of MLD gratings using the raster scan method in order to estimate operational performance. We also report results of R-on-1 tests performed with varying pulse duration (1-30 ps) in air, and clean vacuum. Measurements were also performed in vacuum with controlled exposure to organic contamination to simulate the grating use environment. Results show sparse defects with lower damage resistance which were not detected by small-area damage test methods.

The desire to field space-based telescopes with apertures in excess of 10 meter diameter is forcing the development of extreme lightweighted large optomechanical structures. Sparse apertures, shell optics, and membrane optics are a few of the approaches that have been investigated and demonstrated. Membrane optics in particular have been investigated for many years. The MOIRE approach in which the membrane is used as a transmissive diffractive optical element (DOE) offers a significant relaxation in the control requirements on the membrane surface figure, supports extreme lightweighting of the primary collecting optic, and provides a path for rapid low cost production of the primary optical elements. Successful development of a powered meter-scale transmissive membrane DOE was reported in 2012. This paper presents initial imaging results from integrating meter-scale transmissive DOEs into the primary element of a 5-meter diameter telescope architecture. The brassboard telescope successfully demonstrates the ability to collect polychromatic high resolution imagery over a representative object using the transmissive DOE technology. The telescope includes multiple segments of a 5-meter diameter telescope primary with an overall length of 27 meters. The object scene used for the demonstration represents a 1.5 km square complex ground scene. Imaging is accomplished in a standard laboratory environment using a 40 nm spectral bandwidth centered on 650 nm. Theoretical imaging quality for the tested configuration is NIIRS 2.8, with the demonstration achieving NIIRS 2.3 under laboratory seeing conditions. Design characteristics, hardware implementation, laboratory environmental impacts on imagery, image quality metrics, and ongoing developments will be presented.

The ability to fabricate 4-level diffractive structures with 1 µm critical dimensions has been demonstrated for the creation of fast (∼f/3.1 at 633 nm) Fresnel zone lenses (FZLs) with >60% diffraction efficiency into the -1 focusing order and nearly complete suppression of 0 and +1 orders. This is done using tooling capable of producing optics with 800 mm apertures. A 4-level grating fabricated in glass at 300 mm aperture is shown to have <15  nm rms holographic phase error. Glass FZLs have also been used as mandrels for casting zero-thermal-expansion, 20 µm thick polymer films created with the 4-level structure as a route to mass replication of efficient diffractive membranes for ultralight segmented space-based telescope applications.

The design and fabrication of large-area, high-efficiency metallic gratings for use in high-power laser systems is described. The gratings exhibit a diffraction efficiency in excess of 95% in the m = -1 order (Littrow mount) and have a high threshold for laser damage. Computations and experimental measurements are presented that illustrate the effect of grating shape and polarization on efficiency. A simple theory for optical damage to metallic diffraction gratings is developed and compared with experimental measurements of the laser-damage threshold over the pulse range from 400 fs to >1 ns.

We investigate a plasmonic resonant structure tunable from ultra-violet to near infrared wavelengths with maximum absorbance strength over 95% due to a highly efficient coupling with incident light. Additional harmonics are excited at higher frequencies extending the absorbance range to multiple wavelengths. We propose the concept of a plasmonic black metal nanoresonator that exhibits broadband absorbance characteristics by spacing the modes closer through increasing the resonator length and by employing adiabatic plasmonic nano-focusing on the tapered end of the cavity.

Anti-reflecting (AR) surface relief nano-textures have been integrated with fused silica diffraction gratings to demonstrate the potential of stable diffractive 3ω beam samplers with increased energy to target at the National Ignition Facility (NIF). TelAztec’s AR texturing process was used to etch Random-type AR (RAR) microstructures in sub-scale NIF Grating Debris Shields consisting of large pitch, shallow line gratings. This superposition yielded the desired ~3.5% increase in zero-order transmission uniformly over the full aperture without compromising the grating function. Another fused silica window fabricated with RAR nano-textures in both faces for a 3ω (351nm) transmission of 99.5%, was subjected to capillary condensation tests to evaluate the resistance of the RAR texture to the adsorption of organic compounds. It was found that for a one day exposure time to a surrogate suite of organic contaminants, the RAR textured fused silica surfaces adsorbed less than one fourth the amount of organic contaminants found on a NIF baseline hardened sol-gel AR coated optic. In two additional exposure cycles, further RAR process refinement reduced the amount of adsorbed organics to a level nearly 200 times below the current NIF baseline. Significantly, the 3ω transmission of the RAR textured window remained unchanged after all three exposure cycles, whereas the sol-gel coated windows showed losses up to 4.9% for the highest contaminant concentration. Large beam pulsed laser damage testing of RAR textured fused silica windows was conducted with the Optical Sciences Laser (OSL) at NIF. The RAR sample damage resistance was found to be equivalent to the current NIF baseline - even after multiple aggressive chemical cleaning cycles. Lastly, a series of RAR textured and sol-gel AR coated windows were subjected to commercial 3ω pulsed laser damage testing at Quantel. The results indicate an average RAR damage threshold of 26 J/cm2, a level about 80% of the two NIF fused silica samples tested, two times higher than the best performing ion beam sputtered thin-film AR coatings reported in the literature, and six times higher than catalog high power laser window coating specifications.

Macroscopic porous membranes with pore diameter uniformity approaching the nanometer scale have great potential to significantly increase the speed, selectivity, and efficiency of molecular separations. We present fabrication, characterization, and molecular transport evaluation of nanoporous thin silicon-based sieves created by laser interferometric lithography (LIL). This fabrication approach is ideally suited for the integration of nanostructured pore arrays into larger microfluidic processing systems, using a simple all-silicon lithographic process. Submilli-meter-scale planar arrays of uniform cylindrical and pyramidal nanopores are created in silicon nitride and silicon, respectively, with average pore diameters below 250 nm and significantly smaller standard error than commercial polycarbonate track etched (PCTE) membranes. Molecular transport properties of short cylindrical pores fabricated by LIL are compared to those of thicker commercial PCTE membranes for the first time. A 10-fold increase in pyridine pore flux is achieved with thin membranes relative to commercial sieves, without any modification of the membrane surface.

We present the detection of volatile organic compounds directly in their vapor phase by surface-enhanced Raman scattering (SERS) substrates based on lithographically-defined two-dimensional rectangular array of nanopillars. The type of nanopillars is known as the tapered pillars. For the tapered pillars, SERS enhancement arises from the nanofocusing effect due to the sharp tip on top. SERS experiments were carried out on these substrates using various concentrations of toluene vapor. The results show that SERS signal from a toluene vapor is strongly influenced by the substrate temperature, and the toluene vapor can be detected within minutes of exposing the SERS substrate to the vapor. A simple adsorption model is developed which gives results matching the experimental data. The results also show promising potential for the use of these substrates in environmental monitoring of gases and vapors.

A highly-sensitive optical fiber surface-enhanced Raman scattering (SERS) sensor has been developed by interference lithography. While one facet of the optical fiber is patterned with silver-coated nanopillar array as a SERS platform, the other end of the probe is used, in a remote end detection, to couple the excitation laser into the fiber and send the SERS signal to the spectrometer. SERS performance of the probe is characterized using trans-1,2-bis(4-pyridyl)-ethylene (BPE) monolayer and an enhancement factor of 1.2 × 10(7) can be achieved by focusing the laser directly onto the nanopillar array (front end detection). We also demonstrate that this probe can be used for in situ remote sensing of toluene vapor by the remote end detection. Such a fiber SERS probe shows great potential for molecular detection in various sensing applications.

The desire to field space-based telescopes with apertures in excess of 10 meter diameter is forcing the development of extreme lightweighted large optics. Sparse apertures, shell optics, and membrane optics are a few of the approaches that have been investigated and demonstrated. Membrane optics in particular have been investigated for many years. The majority of the effort in membrane telescopes has been devoted to using reflective membrane optics with a fair level of success being realized for small laboratory level systems; however, extending this approach to large aperture systems has been problematic. An alternative approach in which the membrane is used as a diffractive transmission element has been previously proposed, offering a significant relaxation in the control requirements on the membrane surface figure. The general imaging principle has been demonstrated in 50-cm-scale laboratory systems using thin glass and replicated membranes at long f-number (f/50). In addition, a 5-meter diameter f/50 transmissive diffractive optic has been demonstrated, using 50-cm scale segments arrayed in a foldable origami pattern. In this paper we discuss Membrane Optical Imager Real-time Exploitation (MOIRE) Phase 1 developments that culminated in the development and demonstration of an 80 cm diameter, off-axis, F/6.5 phase diffractive transmissive membrane optic. This is a precursor for an optic envisioned as one segment of a 10 meter diameter telescope. This paper presents the demonstrated imaging wavefront performance and collection efficiency of an 80 cm membrane optic that would be used in an F/6.5 primary, discusses the anticipated areal density in relation to existing space telescopes, and identifies how such a component would be used in previously described optical system architectures.

We present a new class of surface-enhanced Raman scattering (SERS) substrates based on lithographically-defined two-dimensional rectangular array of nanopillars. Two types of nanopillars within this class are discussed: vertical pillars and tapered pillars. For the vertical pillars, the gap between each pair of nanopillars is small enough (< 50 nm) such that highly confined plasmonic cavity resonances are supported between the pillars when light is incident upon them, and the anti-nodes of these resonances act as three-dimensional hotspots for SERS. For the tapered pillars, SERS enhancement arises from the nanofocusing effect due to the sharp tip on top. SERS experiments were carried out on these substrates using various concentrations of 1,2 bis-(4-pyridyl)-ethylene (BPE), benzenethiol (BT) monolayer and toluene vapor. The results show that SERS enhancement factor of over 0.5 x 109 can be achieved, and BPE can be detected down to femto-molar concentration level. The results also show promising potential for the use of these substrates in environmental monitoring of gases and vapors such as volatile organic compounds.

Nano- to micrometer-sized surface defects on UV-grade fused silica surfaces are known to be effectively smoothed through the use of high-temperature localized CO2 laser heating, thereby enhancing optical properties. However, the details of the mass transport and the effect of hydroxyl content on the laser smoothing of defective silica at sub-micron length scales are still not completely understood. In this study, we examine the morphological evolution of sub-micron, dry-etched periodic surface structures on type II and type III SiO2 substrates under 10.6μm CO2 laser irradiation using atomic force microscopy (AFM). In situ thermal imaging was used to map the transient temperature field across the heated region, allowing assessment of the T-dependent mass transport mechanisms under different laser-heating conditions. Computational fluid dynamics simulations correlated well with experimental results, and showed that for large effective capillary numbers (Nc>2), surface diffusion is negligible and smoothing is dictated by capillary action, despite the relatively small spatial scales studied here. Extracted viscosity values over 1700–2000K were higher than the predicted bulk values, but were consistent with the surface depletion of OH groups, which was confirmed using confocal Raman microscopy.

We investigate tunable plasmon resonant cavity arrays in paired parallel nanowire waveguides. Resonances are observed when the waveguide length is an odd multiple of quarter plasmon wavelengths, consistent with boundary conditions of node and antinode at the ends. Two nanowire waveguides satisfy the dispersion relation of a planar metal-dielectric-metal waveguide of equivalent width equal to the square field average weighted gap. Confinement factors over 10(3) are possible due to plasmon focusing in the interwire space.