Transition metal nitrides (TMNs) are emerging as a promising class of materials for application in optoelectronics as well as energy conversion and storage, but they remain rather unexplored, mainly due to a lack of mechanistic understanding of their synthetic pathways. Here, a one-pot synthesis is demonstrated, which yields 3 nm phase-pure Cu3PdN nanoparticles after the reaction of Cu methoxide and Pd acetylacetonate in benzylamine for 5 min at 140 degrees C. The structure of the initial complexes and their conversion to Cu3PdN are revealed by in situ X-ray absorption spectroscopy measurements and elucidate nucleation and growth of the nitride nanocrystals by in situ total X-ray scattering measurements. Interestingly, extended X-ray absorption fine structure double-edge refinement reveals the presence of short-range cation-site disorder in the anti-perovskite structure of Cu3PdN, which has not been observed before in the Cu3PdN system. Additionally, the synthesized Cu3PdN nanoparticles are tested for the electrocatalytic hydrogen evolution reaction, revealing an overpotential as low as eta 10 = 212 +/- 11 mV measured at 10 mA cm-2.

The key to control the fabrication process of transition metal sulfide nanocrystals is to understand the reaction mechanism, especially the coordination of ligands and solvents during their synthesis. We utilize in situ High-Energy Resolution Fluorescence Detected X-ray Absorption Spectroscopy (HERFD-XAS) as well as in situ valence-to-core X-ray Emission Spectroscopy (vtc-XES) combined with Density Functional Theory (DFT) calculations to identify the formation of an octahedral [Zn(OA)6]2+ complex, and the ligand exchange to a tetrahedral [Zn(SOA)4]2+ complex (OA = oleylamine, OAS = oleylthioamide), during the synthesis of ZnS nanorods in oleylamine. We observe in situ the transition of the electronic structure of [Zn(SOA)4]2+ with a HOMO/LUMO gap of 5.0 eV towards an electronic band gap of 4.3 eV and 3.8 eV for 1.9 nm large ZnS wurtzite nanospheres and 2 x 7 nm sphalerite nanorods, respectively. Thus, we demonstrate how in situ multimodal X-ray spectroscopy and scattering studies can not only resolve structure, size, and shape during the growth and synthesis of NPs in organic solvents and at high temperature but also give direct information about their electronic structure, which is not readily accessible through other techniques.

Exciton-phonon coupling limits the homogeneous emission line width of nanocrystals. Hence, a full understanding of this is crucial. In this work, we statistically investigate exciton-phonon coupling by performing single-particle spectroscopy on colloidal Zn1-xCdxSe/CdS and CdSe/CdS dot-in-rod nanocrystals at cryogenic temperatures (T approximate to 10 K). In situ cation exchange enables us to analyze different band alignments and, thereby, different charge-carrier distributions. We find that the relative intensities of the longitudinal optical S- and Se-type phonon replicas correlate with the charge-carrier distribution. Our experimental findings are complemented with quantum mechanical calculations within the effective mass approximation that hint at the relevance of surface charges.

We here investigate how the synthesis method affects the crystallite size and atomic structure of cobalt iron oxide nanoparticles. By using a simple solvothermal method, we first synthesized cobalt ferrite nanoparticles of ca. 2 and 7 nm, characterized by Transmission Electron Microscopy (TEM), Small Angle X-ray scattering (SAXS), X-ray and neutron total scattering. The smallest particle size corresponds to only a few spinel unit cells. Nevertheless, Pair Distribution Function (PDF) analysis of X-ray and neutron total scattering data shows that the atomic structure, even in the smallest nanoparticles, is well described by the spinel structure, although with significant disorder and a contraction of the unit cell parameter. These effects can be explained by the surface oxidation of the small nanoparticles, which is confirmed by X-ray near edge absorption spectroscopy (XANES). Neutron total scattering data and PDF analysis reveal a higher degree of inversion in the spinel structure of the smallest nanoparticles. Neutron total scattering data also allow magnetic PDF (mPDF) analysis, which shows that the ferrimagnetic domains correspond to ca. 80% of the crystallite size in the larger particles. A similar but less well-defined magnetic ordering was observed for the smallest nanoparticles. Finally, we used a co-precipitation synthesis method at room temperature to synthesize ferrite nanoparticles similar in size to the smallest crystallites synthesized by the solvothermal method. Structural analysis with PDF demonstrates that the ferrite nanoparticles synthesized via this method exhibit a significantly more defective structure compared to those synthesized via a solvothermal method.

Exciton-phonon coupling limits the homogeneous emission linewidth of nanocrystals. Hence, a full understanding of it is crucial. In this work, we statistically investigate exciton-phonon coupling by performing single-particle spectroscopy on Zn$_{1-x}$Cd$_{x}$Se/CdS dot-in-rod nanocrystals at cryogenic temperatures ($T\approx 10~\rm{K}$). In situ cation exchange enables us to analyze different band alignments and thereby different charge-carrier distributions. We find that the relative intensities of the longitudinal optical S- and Se-type phonon replicas correlate with the charge-carrier distribution. Our experimental findings are complemented with quantum mechanical calculations within the effective mass approximation that hint at the relevance of surface charges.

Nanozymes are nanomaterials with biocatalytic properties under physiological conditions and are one class of artificial enzymes to overcome the high cost and low stability of natural enzymes. However, surface ligands on nanomaterials will decrease the catalytic activity of the nanozymes by blocking the active sites. To address this limitation, ligand-free PtAg nanoclusters (NCs) are synthesized and applied as nanozymes for various enzyme-mimicking reactions. By taking advantage of the mutual interaction of zeolitic imidazolate frameworks (ZIF-8) and Pt precursors, a good dispersion of PtAg bimetal NCs with a diameter of 1.78 ± 0.1 nm is achieved with ZIF-8 as a template. The incorporation of PtAgNCs in the voids of ZIF-8 is confirmed with structural analysis using the atomic pair-distribution function and powder X-ray diffraction. Importantly, the PtAgNCs present good catalytic activity for various enzyme-mimicking reactions, including peroxidase-/catalase- and oxidase-like reactions. Further, this work compares the catalytic activity between PtAg NCs and PtAg nanoparticles with different compositions and finds that these two nanozymes present a converse dependency of Ag-loading on their activity. This study contributes to the field of nanozymes and presents a potential option to prepare ligand-free bimetal biocatalysts with sizes in the nanocluster regime.

CuBi2 O4 has recently emerged as a promising photocathode for photo-electrochemical (PEC) water splitting. However, its fast degradation under operation currently poses a limit to its application. Here, we report a novel method to study operando the semiconductor-electrolyte interface during PEC operation by surface-sensitive high-energy X-ray scattering. We find that a fast decrease in the generated photocurrents correlates directly with the formation of a metallic Bi phase. We further show that the slower formation of metallic Cu, as well as the dissolution of the electrode in contact with the electrolyte, further affect the CuBi2 O4 activity and morphology. Our study provides a comprehensive picture of the degradation mechanisms affecting CuBi2 O4 electrodes under operation and poses the methodological basis to investigate the photocorrosion processes affecting a wide range of PEC materials.

CuBi2O4 has recently emerged as a promising photocathode for photo-electrochemical (PEC) water splitting. However, its fast degradation under operation currently poses a limit to its application. Here, we report a novel method to study operando the semiconductor-electrolyte interface during PEC operation by surface-sensitive high-energy X-ray scattering. We find that a fast decrease in the generated photocurrents correlates directly with the formation of a metallic Bi phase. We further show that the slower formation of metallic Cu, as well as the dissolution of the electrode in contact with the electrolyte, further affect the CuBi2O4 activity and morphology. Our study provides a comprehensive picture of the degradation mechanisms affecting CuBi2O4 electrodes under operation and poses the methodological basis to investigate the photocorrosion processes affecting a wide range of PEC materials.

Graphene oxide (GO) sheets have been used as a building block to construct various bulk forms of graphene structures such as films, fibers, foams, and dense solids. Thermal reduction of GO, where GO actually undergoes a disproportionation reaction to yield reduced GO (r-GO), accompanied by evolution of carbonaceous gases, has critical influence over the mechanical, thermal, and electrical properties and chemical stability of the resulting bulk graphene solids. Here, we report that this thermal reduction process is geometry-dependent for bulk GO solids, including the peak temperature of reaction, reaction rate, the chemical composition of released gases, and the C/O ratio of the resulting r-GO products, which can be largely attributed to additional reactions between trapped reaction intermediates. The work enriches the knowledge base of GO materials and offers insights for further tuning of the thermal reduction of GO solids to obtain high performance engineering graphene materials.

Functional thin films are commonly integrated in electronic devices as part of a multi-layer architecture. Metal/oxide/metal structures e.g. in resistive switching memory and piezoelectric microelectrochemical devices are relevant applications. The films are mostly fabricated from the vapour phase or by solution deposition. Processing conditions with a limited thermal budget typically yield nanocrystalline or amorphous layers. For these aperiodic materials, the structure is described in terms of the local atomic order on the length scale of a few chemical bonds up to several nanometres. Previous structural studies of the short-range order in thin films have addressed the simple case of single coatings on amorphous substrates. By contrast, this work demonstrates how to probe the local structure of two stacked functional layers by means of grazing incidence total X-ray scattering and pair distribution function (PDF) analysis. The key to separating the contributions of the individual thin films is the variation of the incidence angle below the critical angle of total external reflection, In this way, structural information was obtained for functional oxides on textured electrodes, i.e. PbZr0.53O0.47O3 on Pt[111] and HfO2 on TiN, as well as HfO2-TiOx bilayers. For these systems, the transformations from disordered phases into periodic structures via thermal teatment are described. These examples highlight the opportunity to develop a detailed understanding of structural evolution during the fabrication of real thin film devices using the PDF technique.