Developing an efficient and stable photocathode material for photoelectrochemical solar water splitting remains challenging. Herein, we demonstrate the potential of rutile TiO2 as a photocathode by Rh doping with visible light absorption up to 640 nm and an onset potential of 0.9 V versus the reversible hydrogen electrode. The dopant transforms the rutile host from an n-type semiconductor to a p-type one, as confirmed by the Mott-Schottky curve and kelvin probe force microscopy. Physical and photoelectrochemical analyses further suggest that the doping mechanism is dependent on concentration. Lower levels of dopants generate localized Rh3+, while higher levels favor Rh4+ that interacts more strongly with the O 2p orbitals. The latter is found not only to extend the visible light absorption range but also to facilitate charge transport. This work elucidates the role of the Rh dopant in adjusting the photoelectrochemical behavior of TiO2, and it provides a promising photocathode material for solar energy conversion.

The intra-gap states that are introduced into a semiconducting photocatalyst via dopants and other defects have significant implications on the transport dynamics of photoexcited electrons and holes during an aqueous light-driven reaction. In this work, mechanistic understanding of Rh-doped rutile, a promising photocatalyst for hydrogen production from water, is gained by systematic assessment combining intensity-modulated photocurrent spectroscopy with sub-gap excitations and alternating-current photocurrent spectroscopy. These operando techniques not only help in discovering a new electronic transport path in Rh-rutile via surface Rh4+ species and elucidating complex interaction between electrolyte molecules and semiconductors, but also underscore the potential of utilizing multiple sub-gap excitations synergistically. This combination offers a powerful tool for acquiring insight into photo-physical and photo-chemical behaviors of photo(electro)catalysts with intra-gap states.

The built-in potential in the space charge layer dominates migration of charge carriers in a traditional photoelectrode model. In this work, through particle engineering and surface reconstruction, a Rh-doped rutile TiO2 (Rh-TiO2) photoelectrode is fabricated, in which the Rh concentration is decreased gradiently in TiO2 particle directed from conductive substrate to solution. Since the Rh dopants involve intragap states above the valence band of TiO2, it shapes a built-in potential that orients the migration of photoexcited holes toward substrate and repels the electrons to solution side, which change the Rh-TiO2 electrode from photoanode to photocathode. Comparison of intensity modulated photocurrent spectroscopy (IMPS) results using ultraviolet and visible light across a wide potential window unveils the different roles of dopants in charge dynamics. The operando chemical status of Rh is further verified by spectroelectrochemical characterization. The present strategy of directional doping not only is conducive to improving electron-hole separation but also provides a new approach to unleash the potential of a semiconductor as both photoanode and photocathode.

Photo-assisted ion batteries utilize light to boost capacity but face cycling instability due to complex charge/ion transfer under illumination. This study identified photo-induced proton transfer (photo-induced PT) as a significant process in photo-(dis)charging of widely-used V2O5-based zinc-ion batteries, contributing to enhanced capacity under illumination but jeopardizing photo-stability. Photo-induced PT occurs at 100 ps after photo-excitation, inducing rapid proton extraction into V2O5 photoelectrode. This process creates a proton-deficient microenvironment on surface, leading to repetitive cathode dissolution and anode corrosion in each cycle. Enabling the intercalated protons from photo-induced PT to be reversibly employed in charge-discharge processes via the anode-alloying strategy achieves high photo-stability for the battery. Consequently, a ~54 % capacity enhancement was achieved in a V2O5-based zinc-ion battery under illumination, with ~90 % capacity retention after 4000 cycles. This extends the photo-stability record by 10 times. This study offers promising advancements in energy storage by addressing instability issues in photo-assisted ion batteries.

The synthesis of photocatalysts with both broad light absorption and efficient charge separation is significant for a high solar energy conversion, which still remains to be a challenge. Herein, a narrow-bandgap Y2Ti2O5S2 (YTOS) oxysulfide nanosheet coexposed with defined {101} and {001} facets synthesized by a flux-assisted solid-state reaction was revealed to display the character of an anisotropic charge migration. The selective photodeposition of cocatalysts demonstrated that the {101} and {001} surfaces of YTOS nanosheets were the reduction and oxidation regions during photocatalysis, respectively. Density functional theory (DFT) calculations indicated a band energy level difference between the {101} and {001} facets of YTOS, which contributes to the anisotropic charge migration between them. The exposed Ti atoms on the {101} surface and S atoms on the {001} surface were identified, respectively, as reducing and oxidizing centers of YTOS nanosheets. This anisotropic charge migration generated a built-in electric field between these two facets, quantified by spatially resolved surface photovoltage microscopy, the intensity of which was found to be highly correlated with photocatalytic H2 production activity of YTOS, especially exhibiting a high apparent quantum yield of 18.2% (420 nm) after on-site modification of a Pt@Au cocatalyst assisted by Na2S-Na2SO3 hole scavengers. In conjunction with an oxygen-production photocatalyst and a [Co(bpy)3]2+/3+ redox shuttle, the YTOS nanosheets achieved a solar-to-hydrogen conversion efficiency of 0.15% via a Z-scheme overall water splitting. Our work is the first to confirm anisotropic charge migration in a perovskite oxysulfide photocatalyst, which is crucial for enhancing charge separation and surface catalytic efficiency in this material.