X-ray topography has been used to study single crystal diamond samples homoepitaxially grown by microwave plasma-assisted chemical vapour deposition (CVD) on high pressure high temperature (HPHT) and CVD synthetic diamond substrates. Clusters of dislocations in the CVD diamond layers emanated from points at or near the interface with the substrate. The Burgers vectors of observed dislocations have been determined from sets of {111} projection topographs. Dislocations have line directions close to the [001] growth direction and are either edge or 45° mixed dislocations. Where groups of dislocations originated at isolated points they tended to be of the edge variety. Where the substrate surface was deliberately damaged before growth, two sets of dislocations were observed to have propagated from each line of damage and there was a tendency for dislocations to be of the 45° mixed variety with a component of their Burgers vector parallel to the polishing direction. It is demonstrated that X-ray topography can be used to deduce the growth history of CVD synthetic diamond samples produced in multiple growth stages.

Studies carried out at the DTC Research Centre have shown that single-crystal CVD synthetic diamond is clearly distinguishable from natural diamond. This article presents information about the CVD process, the history of its development, the different kinds of CVD synthetic diamond material that can be produced, and properties that differentiate them from natural diamond. The authors studied more than a thousand CVD synthetic diamond samples that were grown for research purposes using a range of different process conditions. Absorption, photoluminescence, and cathodoluminescence spectra of these CVD synthetic diamond samples showed a range of different impurity-related features not seen in natural diamond. Photoluminescence imaging is also useful in identifying CVD synthetic diamond, and X-ray topography may give supportive evidence. The effectiveness of the Diamond Trading Company Diamond Verification Instruments for identifying CVD synthetic diamond is also described.