Asphalt is a kind of high viscosity material with fluidity under certain conditions, which results in the healing function to repair small cracks of asphalt pavement by itself, and thus prolonging the service life of the pavement. With the aging process, the flow behavior of asphalt will gradually deteriorate and synchronously impact the self-healing performance. To gain a deeper understanding of the changes in asphalt's performance characteristics after aging, Fourier transform infrared spectroscopy tests, Frequency scanning tests, and Fatigue-healing-fatigue tests were conducted to examine the changes in flow behavior and self-healing properties of asphalt enduring secondary aging. The results showed that SBS modified asphalt presented superior anti-aging performance compared to base asphalt, since the SBS modifier can effectively prevent the formation of sulfoxides and carbonyl groups in asphalt. However, SBS modifier will also inhibit the flow behavior of asphalt due to its complex three-dimensional spatial structure, leading to a decrease in flow behavior index from 0.967 for unaged base asphalt to 0.672 for SBS modified asphalt, respectively. Furthermore, both of the flow behavior and self-healing performance will be affected by aging process. After secondary aging, the flow behavior index of base and SBS modified asphalt decreased by 9.8% and 12.1% compared to the corresponding virgin asphalt mastics, respectively, while the self-healing performance decreasing by 83.9% and 57.6%. These findings provide an innovative perspective for secondary recycling research and application of asphalt pavements.

In the context of green and low-carbon development, energy saving, and emission reduction, hot recycling technology (RT) has been researched, which is divided into hot central plant RT and hot in-place RT. However, due to the aged asphalt binders, the shortcomings of hot recycled asphalt mixtures have become apparent, as in comparison to new asphalt mixtures, their resistance to cracking was inferior and the cracking resistance deteriorated more rapidly. Therefore, it was very necessary to focus on the improvement of crack resistance of hot recycled asphalt mixtures. Basalt fiber has been proved to be able to effectively improve the comprehensive road performance of new asphalt mixtures. Therefore, this paper introduced basalt fiber to hot central plant recycled and hot in-place recycled asphalt mixtures, in order to improve the crack resistance of asphalt as a new type of fiber stabilizer. Firstly, six types of SMA-13 fiber asphalt mixtures were designed and prepared, i.e., hot mixtures with basalt fiber or lignin fiber, hot central plant recycled mixtures with basalt fiber or lignin fiber, and hot in-place recycled mixtures with basalt fiber or lignin fiber. Secondly, the trabecular bending test, low-temperature creep test, semi-circular bending test, and IDEAL-CT were used to comparatively study the changing patterns of low and intermediate temperature cracking resistance of hot recycled mixtures with conventional lignin fibers or basalt fibers. Finally, Pearson’s correlation coefficient was used to analyze the correlation of the different cracking resistance indicators. The results show that the low and intermediate temperature cracking resistance of hot central plant recycled mixtures increased by 45.6% (dissipative energy ratio, Wd/Ws) and 74.8% (flexibility index, FI), respectively. And the corresponding cracking resistance of hot in-place recycled mixture increased by 105.4% (Wd/Ws) and 55.7% (FI). The trabecular bending test was more suitable for testing the low-temperature cracking resistance of hot recycled asphalt mixtures, while the IDEAL-CT was more suitable for testing the intermediate-temperature cracking resistance. The results can provide useful references for the utilization of basalt fiber in the hot recycling of SMA-13 asphalt mixtures.

Reclaimed asphalt pavement (RAP) has been widely utilized because it is an environmentally friendly and economical material. The performance of recycled asphalt mixtures will deteriorate gradually with the secondary aging process of asphalt, including the self-healing property. To further understand the self-healing characteristics of asphalt after secondary aging, taking 70# petroleum asphalt, SBS-modified asphalt, and extracted old asphalt mastics as objects, the fatigue self-healing test and fracture self-healing test were conducted to simulate the intermediate-and low-temperature healing behaviors of different asphalt mastics. The impact of healing time, healing temperature, and aging degree of mastics on the healing performance was systematically investigated. The results show that the original unaged asphalt mastics present excellent fatigue healing properties with an index of 0.796 and 0.888 for 70# petroleum and SBS-modified asphalt mastics, respectively. The secondary aging process causes significant impact on the healing properties, leading to a great drop in the corresponding index, which decreased to 47.5% and 72.5% of that of the unaged ones. The fracture healing ability of all mastics was much inferior to the fatigue healing. After secondary aging, the fracture healing index values of 70# petroleum asphalt, SBS-modified asphalt, and extracted old asphalt mastics were all as low as around 0.3, indicating similar performance can be found in the secondary aged SBS-modified asphalt mastics and 70# asphalt mastics. Overall, after secondary aging, the fatigue damage of SBS-modified asphalt mastics can be cured effectively by self-healing, but the fatigue and fracture self-healing properties of 70# asphalt mastics are difficult to recover. These results could provide an innovative view to understand the fatigue and fracture healing characteristics of recycled asphalt pavement after secondary aging.

The performance improvement of hot in-place recycling asphalt mixtures has been a hot topic recently due to the widespread application of HIP recycling technology. Based on the maintenance project of the provincial pavement G233 Baoying section, basalt fibers were introduced into HIP recycling mixtures. The effect of basalt fiber on the comprehensive performance of recycled mixtures was investigated using high temperature stability tests, cracking resistance tests, water stability tests, and dynamic modulus tests. Moreover, the performance of site mixtures was comparatively investigated with that of lab-made mixtures to further explore the site mixing effect on the mixture performance. The results showed that the recycled mixtures without basalt fiber presented unqualified cracking resistance even though proper mixture design was performed. The addition of basalt fibers could greatly enhance the rutting resistance, low-temperature cracking resistance, and stripping resistance of HIP recycled mixtures by 105.2%, 102.3%, and 46.9%, respectively. Moreover, the mixing method also had a significant impact on the properties of mixtures. The recycled mixtures produced by the site re-mixing method showed inferior performance compared to that of mixtures produced by the lab mixing method. Specifically, the dynamic stability, low temperature failure strain, and stripping point values reduced by 44.1%, 16.2%, and 11.7%, respectively, indicating that the site re-mixing process was not as effective as the lab mixing process due to the weaker blending and mixing procedures of the site equipment. The results could be beneficial for the utilization of basalt fiber in HIP recycling technology.

Adding basalt fiber (BF) can effectively enhance the performance of asphalt mixtures and improve the service quality of asphalt pavement. However, the effect of BF on the high-temperature performance of different types of asphalt mixtures and systematic high-temperature performance test analysis are still not well known. To address this issue, three typical types of asphalt mixtures of AC-13, SMA-13, and SUP-13 were selected. Wheel tracking test, uniaxial penetration test, dynamic modulus test, and dynamic creep test were conducted. In addition, relevant parameters of dynamic stability, penetration strength, dynamic modulus index, and flow number were analyzed. The results showed that adding BF into the asphalt mixture could improve the dynamic stability, penetration strength, dynamic modulus index, and flow number significantly, indicating that adding basalt fiber is an effective solution to the rutting deformation damage of asphalt pavement. Moreover, the parameter of dynamic stability presented an approximate polynomial correlation with penetration strength, dynamic modulus index, and flow number, respectively. These findings provide a certain theoretical reference for evaluating the high-temperature performance of BF-modified asphalt mixtures.

A new type of plastic and basalt fiber composite (PB) modifier, which is composed of waste plastic and basalt fiber using a specific process, was used for bus lanes to address severe high-temperature deformation diseases due to the heavy loads of buses. The dense gradations of asphalt mixture with a nominal maximum aggregate size of 13.2 mm (AC-13) and 19 mm (AC-20) were selected to fabricate asphalt mixtures. The impact of the modifier PB on the high-temperature rutting resistance, low-temperature crack resistance, and water damage resistance was investigated experimentally. The experimental results showed that adding the modifier PB could enhance the rutting resistance and water damage resistance of asphalt mixtures significantly while maintaining the low-temperature crack resistance. Then, PB-modified asphalt mixtures of AC-13 and AC-20 were employed into a typical pavement structure of a bus lane in Yangzhou city, China, and three types of designed pavement structures were proposed. On this basis, statics analyses of all of the designed structures were performed using the finite element method. The statics analyses revealed that, compared with the standard axle load, the actual over-loaded axle made the pavement structure of the bus lane suffer a 30% higher stress and vertical deformation, leading to accelerated rutting damage on the bus lanes. The addition of the modifier PB could make the pavement structure stronger and compensate for the negative effect caused by the heavy axle load. These findings can be used as a reference for the pavement design of urban bus lanes.

To explore the effect of ultraviolet (UV) aging on the adhesion properties of warm mix asphalt (WMA), WMA binders were prepared by adding Evotherm M1 and Sasobit into base asphalt. The base asphalt and two WMA binders were aged using a self-made UV aging box after a rolling thin-film oven test (RTFOT). As a comparison, pressure aging vessel (PAV) tests were performed for asphalt binders after RTFOT. The contact angles between the WMA binder and distilled water, glycerol, and formamide, before and after UV aging, were measured using the sessile drop method. On the basis of the surface free energy (SFE) theory, the SFE and its components, cohesion work, adhesion work, peeling work, and compatibility rate, before and after the UV aging of WMA, were obtained. The results show that the contact angle between WMA and water gradually increases with the degree of UV aging, which indicates that the aging increases the hydrophobicity of asphalt. After the RTFOT aging, UV aging at different times, and PAV aging, the SFE and its component, as well as cohesion work for all asphalt binders were reduced. The attenuation was severe after UV aging, followed by PAV aging and RTFOT aging. With the extension of UV aging time, the adhesion work, hot mix asphalt, and limestone aggregate compatibility rate gradually reduced, the peeling work increased, and the overall adhesion performance became poor. Under the aging effect of RTFOT and PAV, the Evotherm M1 WMA had the strongest anti-peeling ability, better compatibility, and the best adhesion. When the UV aging time of Sasobit WMA reached 100 h, the adhesion performance increased.