We assessed the biocompatibility of nano-sized ceramic particles with several cells types. Though these particles have less than 100 nm in diameter, they act as submicron-sized particles in saline by aggregation that was estimated using laser diffraction particle size analysis (LDS). they act as submicro-sized particles in saline by aggregation based on laser diffraction particle size analysis (LDS). Several types of cells (osteoblasts, osteosarcoma and hepatocyte cells) were exposed to these particles and their cytocompatibility was estimated. Not only the cytotoxic assay but also their static and dynamic morphology under nanoparticles exposure were investigated. The intercellular uptake of particles was determined using a confocal fluorescence microscope. The particles used in this study did not inhibit cellular activity or growth even when their concentrations were high. Only copper oxide particles caused acute cytotoxicity depending on the particle size. The cytotoxicity assay, dynamic behavior of the nanoparticle-exposed cells and their examination under a confocal fluorescence microscope suggests that the irritative reaction was induced by contact between the cells and particles, whereas eluted copper ions are not dominant factor. These results indicate that nano-sized particles used in this study have excellent biocompatibility except copper oxide ones.

In this study, we prepared two types of europium (Eu)-doped nanoparticle, yttoria and titania and investigated their photo-physical properties and biocompatibilities. These particles do not inhibit cell culture, even at higher concentrations. The obtained nanoparticles had a strong and narrow red photo-luminescent peak. The narrow emission was observed even when the particles were uniformly doped into a polymer film. These results suggest that they can be used for applications not only in optoelectronic devices but also in biomedical devices for bioimaging and luminescent biomedical materials. (C)2014 The Ceramic Society of Japan. All rights reserved.

In this study, we produced europium-doped yttoria (Y2O3:Eu) nanoparticles and investigated their photoluminescent properties and biocompatibility. The Y2O3:Eu nanoparticles showed excellent photoluminescent properties and cytocompatibility. We also analyzed the photophysical properties of the nanoparticles in PMMA films. When the Y2O3:Eu nanoparticles were incorporated in the polymer film, they showed a strong red emission spectrum, similar to that seen with the particles alone. Energy dispersive X-ray spectroscopy (EDS) measurements indicated that the particles were distributed homogeneously in the PMMA film. Such materials could be applied not only to optoelectronic devices but also to biomedical applications such as bioimaging tools or luminescent medical/dental adhesive materials.

Transparent poly(methyl methacrylate)/organically modified montmorillonite (PMMA/OMMT) nanocomposites were fabricated using a solution intercalation method. Two grades of OMMT modified with quaternary alkylammonium ions and containing different amounts of organic matter, NZ70 and NX, were used. X-ray diffraction patterns showed that the peaks regarded as a (0 0 1) d-spacing and a second peak were shifted toward lower 2 theta values, implying the expansion or the partial exfoliation of the silicate layers, respectively. TEM images showed that the silicate platelets were largely well dispersed independent of the hydrophobicity, although some aggregates were observed. The flexural modulus of the PMMA/OMMT nanocomposites increased favorably with an increasing amount of OMMT of either grade. However, only the NX displayed comparable strain at breakage to that of the PMMA. These results suggest that the highly hydrophobic grade NX shows great promise for use in nanocomposites made via solution intercalation. (c) 2012 Elsevier B.V. All rights reserved.