In order to improve the extraction rate and utilization rate of collagen in sheepskin, sheepskin collagen was extracted by acid enzyme compounding method, and collagen-based nanofibers were prepared by electrospinning technology. Taking the extraction rate of sheepskin collagen as the evaluation index, the effects of four factors, namely material-liquid ratio, acetic acid concentration, pepsin concentration and enzymatic hydrolysis time, on the extraction effect of sheepskin collagen were investigated, and the optimal level of single factors was determined. On this basis, the process conditions of sheepskin collagen extraction were optimized by orthogonal experimental design. The effects of enzymatic hydrolysis on the structural properties of collagen were explored by biochemical techniques such as ultraviolet spectrum scanning, infrared spectrum scanning, SDS-PAGE mapping and scanning electron microscopy. Collagen and polylactic acid were then compounded and electrospun to obtain collagen-based nanofibers. The results showed that the best process for extracting sheepskin collagen by acid enzyme compounding method was as follows: Material-liquid ratio of 1:25 g/mL, acetic acid concentration of 1.2 mol/L, pepsin dosage of 1.0%, enzymatic hydrolysis time of 72 h. Under these conditions, the extraction rate of sheepskin collagen was 38.42%±0.49%. Ultraviolet spectroscopy showed that sheepskin collagen had a maximum UV absorption peak around 230 nm. Infrared spectrum scanning and SDS-PAGE map analysis showed that sheepskin collagen was mainly composed of α1, α2 and β three subunit components, which belonged to type I collagen, and the spatial structure of collagen was intact. Scanning electron microscopy showed that the fiber network structure of sheepskin collagen was relatively intact. The collagen-based nanofibers obtained by electrospinning had a diameter of 418.02±183.77 nm, a tensile strength of 3.616±0.386 MPa, and an elongation at break of 8.69%±1.95%, which had excellent physical properties and the potential to be used as a cell scaffold. This study provided a theoretical basis for improving the high-value utilization of sheepskin and sheepskin collagen, and also provided theoretical support for the development of collagen-based nanomedical fiber products.
将精梳大麻与棉纤维通过赛络纺纱方法进行混纺,研究混纺比对精梳大麻/棉混纺纱断裂强度、断裂伸长率、条干、纱疵、毛羽等指标的影响.结果表明:随着大麻纤维占比增大,纱线断裂强度和伸长率总体呈下降趋势,条干不匀率增加,纱线疵点(细节、粗节、麻粒)数量逐渐增多,毛羽增多.综合分析得出,当精梳大麻/棉混纺比为20/80时,混纺纱的综合性能较好.
通过生物还原法制备了杨梅素纳米银粒子,经测定,杨梅素纳米银粒子在近407 nm处存在明显的SPR峰.不同pH值条件下制备的杨梅素纳米银粒子在SPR峰、粒径分布和催化性能方面存在一定差异.随着反应溶液pH值的增大,其SPR峰发生了一定程度的蓝移.当使用杨梅素纳米银粒子催化降解直接紫1染料时,具有较小平均粒径的MP2(pH值为7.013)杨梅素纳米银粒子表现出最佳的催化效率,经过40 min的反应后,直接紫1染料的降解百分率达到82％.
为了纺制高品质聚乙醇酸(PGA)长丝,研究了熔融纺丝工艺路线中全流程纺丝工艺参数,包括泵供量、纺丝速度、热拉伸倍数对PGA长丝力学性能的影响,并结合直径、结晶度、取向度等数据确定了最佳的纺丝工艺.研究了 PGA初生纤维和牵伸纤维的体外降解性能.试验结果表明:当泵供量为22 mL/min,纺丝速度为600 m/min,热拉伸倍数为5.0时,PGA长丝的断裂强度达到6.09 cN/dtex,断裂伸长率为24.26％;纤维的结晶度越高,相同降解时间内质量损失率越小.
产业融合是新时代经济发展的主流趋势之一,产业融合有助于提高相关产业的市场竞争力,推动产业的升级转型并孕育出新的经济增长点,优化产业基础建设,构建高效的产业发展模式,更好的适应旅游与服装消费市场需求变化并催生出新业态.文化旅游产业的综合性等特点为服装产业与文化旅游产业的融合发展打下了基础.服装产业与文化旅游产业的融合为相关产业的发展开启了新道路,通过强化文化旅游产业的带动作用,促进了服装产业的消费多元化.由危华著、浙江大学出版社出版的《我国服装产业国际市场势力构建研究——基于全球价值链视角》一书,阐述深刻、理论丰富,立足全球价值链视角,从国际市场站位对中国服装产业发展开展了系统研究,为服装产业与文化旅游产业的融合发展提供了丰富的研究资料.
丝素蛋白取材广泛,由α-螺旋与β-折叠构成3种晶型结构,具有良好的机械性能与低毒性,物化可塑性与生物相容性强,其复合材料可应用于医用辅料、药物传输、组织工程、传感材料等领域.综述了丝素蛋白及其复合材料在医用敷料、组织工程、药物传递等领域的应用进展,分析了丝素蛋白可用作药物包衣、微球、成膜、纳米纤维、支架等医用载体并可应用于人体组织工程修复与控制药物传递释放等领域.认为:丝素蛋白及其复合材料在医药领域有着广阔的应用前景.
阐述了现有牛角瓜纤维拉伸性能测试方法的基本操作过程,重点就取样工具、制样方法和有效数据等问题进行了分析.通过测试不同夹持位置的牛角瓜纤维的拉伸性能,从结果稳定性和准确性角度出发,确定测试其拉伸性能的最佳位置,并将测试结果与文献中牛角瓜纤维的拉伸性能进行对比.结果表明:选用软头硅胶镊子夹取牛角瓜纤维不易造成纤维损伤;相比"纸夹法"制样,GB/T 14337-2008中的制样方法测得的牛角瓜纤维拉伸性能结果更稳定和准确;测试最佳位置为张力夹钳口距下夹持端下沿1 mm左右.优化后的测试方法也为修订牛角瓜纤维拉伸性能测试标准奠定了基础.
防护纺织品在医疗卫生、军事防护、消防、户外运动服装等领域有着广泛的应用,膜材料在防护纺织品结构中起到核心防护作用.介绍了防护纺织品常用膜材料的种类与特点,阐述了静电纺纳米纤维膜和智能材料的应用.多功能膜材料赋予防护纺织品优异的防水、防血液渗透、抑菌、防有机污染物、防化学毒物及隔离细菌和病毒等特性,必将在防护纺织品中发挥关键作用.
当前社会,世界文化多元并存,西方文化对中华优秀传统文化产生冲击,中华优秀传统文化思想的影响力有所减弱.在这样的背景下,中国不断的提倡发展传统文化,发扬优秀传统文化,将优秀的传统思想文化价值赋予各种产品,以推动优秀传统文化复兴,增强中华文化的世界影响力.因此,挖掘优秀传统文化,弘扬优秀传统思想,将其丰富深厚的思想文化内涵以多种形式展现出来势在必行.
针对自闭症儿童易走失和溺水的问题,设计了一款具有防走失和溺水救生功能的自闭症儿童智能服装.首先针对自闭症儿童的智能穿戴设备进行了相关调研;其次从服装技术系统、服装设计分析两方面进行了整体方案设计;最后通过试验对技术系统的稳定性进行测试.研究表明,基于北斗定位模块的自闭症儿童智能服装能够在儿童走失与溺水时起到保护作用,为特殊儿童智能服装的设计提供借鉴和参考.
利用静电纺丝方法制备聚酰胺(PA)/石墨烯(GO)复合纤维,研究了氧化石墨烯掺杂量、纺丝液质量分数、纺丝电压、纤维接受距离、推进速率等工艺参数对纤维形貌的影响.研究表明,最佳的纺丝工艺条件为:PA质量分数21％(1.5％GO),纺丝电压23.8 kV,接受距离16 cm,推进速率3.6 mm/h.GO的掺杂会改善PA纤维的力学性能和抗紫外性能.当薄膜GO质量分数为1.5％时,其杨氏模量从5 768 MPa提高到8 088 MPa;薄膜GO质量分数为2％时,薄膜UPF值超过30,具有较好的抗紫外效果.
在多巴胺原位聚合的辅助下,调整氧化石墨烯浓度对等离子体处理后的黏胶织物进行整理,并利用防紫外线、导电、电磁辐射屏蔽效能与服用性能指标对整理前后黏胶织物的功能性与可穿性进行表征.测试结果表明:当使用7.5 g/L的氧化石墨烯对黏胶织物进行整理时,织物UPF值高于50,UVA透过率低于0.5;当使用15 g/L的氧化石墨烯对黏胶织物进行整理时,黏胶织物的静电压与半衰期值均达到最低值,对10 MHz电磁辐射的屏蔽效能大于20 dB,且未影响黏胶织物的可穿服用性能.综合分析认为,使用15 g/L的氧化石墨烯对等离子体处理黏胶织物进行整理,可在不影响织物服用性能的前提下,赋予织物优异的防紫外线、导电与电磁辐射屏蔽性能.
随着新时期社会经济和信息技术的不断发展,大众生活品质和审美素养大幅度提升,这一发展态势为服装行业的发展和创新提供了广阔的发展机遇与设计空间,各种风格的服装层出不穷,不仅引领了现代服装设计发展,而且影响了社会大众的服装审美理念.表演服装是服装美学理念在现代艺术领域的体现,是其在服装与艺术领域的融合发展中衍生出的一种新的服装品类,在当前服装领域占有重要地位.相比普通服装来说,钢琴演奏表演服装是服装美学理念的一种独特体现,具有鲜明的艺术创造性和独特功能,是钢琴演奏者精神和情感的外在表达,是钢琴演奏至关重要的构成.钢琴演奏以钢琴为主要载体,灵活运用各种艺术表达手段和演奏技巧与舞台画面、思想情感等有机融合,再以钢琴旋律的形式呈现给观众.从内涵和本质而言,钢琴演奏与服装美学在艺术理念等方面具有较多相似之处,都是艺术审美和情感思想最直观的表达.据此可得,服装美学与钢琴演奏的碰撞与交融能够产生独特的艺术效果.由郭海燕著、北京理工大学出版社出版的《服装与表演艺术》一书,深入研究了服装设计和表演艺术的深度融合.
针对亚麻纤维中果胶的定量测试方法较多,但各方法准确度差异较大的问题,采用质量法、咔唑比色法、硫代硫酸钠滴定法对果胶含量进行测试和比较,探究测试亚麻纤维中果胶定量的最佳方案.研究表明,采用咔唑比色法定量分析亚麻纤维中的果胶含量最准确,具体试验方案为:亚麻试样在回流4～6次/h的条件下经丙酮提取4 h;先后使用10 g/L和5 g/L草酸铵溶液回流煮沸3 h和2 h;采用盐酸乙醇溶液沉淀果胶提取物;最后使用热氨水溶液制备待测溶液,并采用咔唑比色法测试得到果胶含量.
为丰富双贾卡提花间隔鞋材的外观与组织结构设计,提升鞋材的轻薄透气性能,借鉴经编无缝内衣"无底网"成形技术,提出一种利用贾卡梳反向对拉垫纱的原理实施提花间隔鞋材的开发思路.阐述了反向对拉垫纱的工艺原理、鞋材织物的设计步骤和后整理工艺;结合产品开发实例介绍了原料选择、组织设计、花型结构设计、工艺参数、上机织造等各关键工艺.试验结果表明,基于反向对拉垫纱技术的双贾卡提花间隔鞋材轻盈细腻,透气、透湿性良好,外观新颖时尚,可作为休闲运动鞋面的优选材料,同时为经编双贾卡鞋面材料的开发提供参考.
通过单因素试验分析确定复合纺织面料中丝的最佳溶解工艺,探讨了不同的溶解时间、浴比及溶解温度对丝组分溶解的影响,采用化学溶解法对复合面料进行溶解.先用氯化钙-乙醇-水体系溶解丝麻复合面料中的丝组分,观察溶解丝组分是否对麻纤维有影响,再将丝组分溶解液制成再生丝素蛋白海绵,并对再生产物进行红外光谱、XRD、接触角和热学性能表征.结果表明:丝的最优溶解工艺为以摩尔比1∶ 2∶ 8的氯化钙-乙醇-水作为溶剂,丝与溶剂的浴比为1∶ 25,在温度80℃下溶解60 min;此溶解工艺并没有损伤剩余麻组分,经溶解后的丝组分回收产物可进行再利用.
基于目前废旧纺织品回收行业存在的分拣效率低、分拣准确率低等问题,研发了一套废旧纺织品自动鉴别分拣设备.采用DA200在线近红外光谱仪与工业控制计算机(DT-5206-IH61MB)相结合的方式设计了废旧纺织品自动鉴别分拣设备.重点介绍了整套设备在结构组成、装备设计、软件算法部分及分拣效果等方面的关键技术.该设备不仅能持续、高效地分拣纺织品,还可以连续运行48 h以上,传送带速度为0.8 m/s,可分拣1 500～2 000件/h,经过验证其综合分拣准确率可以达到89％.废旧纺织品自动鉴别分拣设备的研发为纺织回收企业大大节约了劳动力成本,并提高了废旧纺织品的分拣效率,实现了高效、节能、安全的分拣.
构建了用于检测布匹经纬位置的整体设计方案,基于设计方案对系统的关键硬件如光学成像模块、前端采集模块、位置测算模块等进行了选型和设计,基于Microsoft Visual C++6.0平台开发了用于控制硬件系统的软件.试验结果表明,所开发的系统对布匹经纬位置具有很好的定位和识别能力.
从结构设计安全性、内在质量要求、外观质量要求和使用说明等方面,介绍了 GB/T 41902-2022《哺乳装》的具体要求.通过对其技术指标进行分析得出结论,GB/T 41902-2022中安全性能达到婴幼儿产品标准要求,同时满足哺乳期母婴需求,研究结果为哺乳服装的设计研发及生产质量控制提供参考.
鉴于传统夏季单面织物存在尺寸稳定性差、易卷边的缺点,以内外层润湿梯度效应为基础,对织物组织结构进行变换开发,设计了 4种不同组织结构的具有吸湿排汗功能的双面小网眼系列织物.通过透气透湿以及织物液态水分管理测试,对织物的吸湿排汗性能进行综合评价.研究结果表明:双面小网眼组织的织物具有良好的吸湿排汗效果,可满足夏季运动休闲面料的要求;双面小网眼织物的网眼孔隙越大,网眼密度越高,织物透气性越好;网眼的孔隙越大,织物的透湿性越好;不同的织物组织结构达到的吸湿排汗效果会有所差异.