Waterborne polyurethane coatings without the flame retardant treatment are flammable, so the research about the flame retardant waterborne polyurethane is an important research direction. The classification of waterborne polyurethane flame retardant coatings was introduced. Flame retardant coatings can be categorized as blending and reactive compound, intumescent and non-intumescent according to different classification criteria. Flame retardant effect and flame retardant mechanisms of waterborne polyurethane flame retardant coatings were discussed and the research of intumescent flame retardant polyurethane coatings was highlighted. Finally, the problems which waterborne intumescent flame retardant polyurethane coating existed and the trends of waterborne intumeseent flame retardant polyurethane coatings development are were proposed.
以聚醚三醇330N和聚碳酸酯二醇(PCDL)混合多元醇为软段、4,4′-二苯基甲烷二异氰酸酯(MDI)为异氰酸酯组分、乙二醇(EG)和1,4-丁二醇(BDO)为混合扩链剂,采用预聚法制备了聚醚/聚酯基聚氨酯弹性体(PUE).讨论了EG/BDO质量比对PUE微相分离结构、刚性、阻尼性能、热稳定性及力学性能的影响.结果表明,随着EG含量增加,PUE的微相分离程度增加,刚性增加,阻尼性能提高;引入EG扩链剂后,PUE的热稳定性降低;当EG/BDO质量比为70∶30 时,所得PUE综合力学性能较优.
为了解决溶剂型冷补混合料强度形成慢、水稳定性和耐久性差等问题,选择聚氨酯预聚体作为胶结料分别制备聚氨酯冷补混合料AC-13(A1)和LB-13(A2),选择聚氨酯预聚体和沥青制备聚氨酯改性沥青,再分别制得聚氨酯改性沥青冷补混合料AC-13(B1)和LB-13(B2),通过室内试验对其路用性能开展研究.结果表明:AC-13(A1)的动稳定度、残留稳定度比、冻融劈裂强度比和最大破坏应变分别达到54321 次/mm、91.0%、88.2%和 5105 με,AC-13(B1)的动稳定度、残留稳定度比、冻融劈裂强度比和最大破坏应变分别达到23545 次/mm、89.9%、84.6%和3657 με,AC-13(A1)相比于AC-13(B1)、LB-13(A2)和LB-13(B2)的动稳定度、残留稳定度比、冻融劈裂强度比和最大破坏应变均较高.AC-13 相比于LB-13 冷补混合料的路用性能较优,并且采用聚氨酯预聚体制备的AC型冷补混合料路用性能最优.
以聚己二酸乙二醇酯二醇(PEA)、1,5-萘二异氰酸酯(NDI)、二苯基甲烷二异氰酸酯(MDI)及扩链剂1,4-丁二醇为原料,采用预聚体法合成聚氨酯弹性体(PUE),研究了NDI/MDI质量比对PUE常温及高温下力学性能、热性能、动态力学性能等性能的影响.结果表明:随着NDI/MDI质量比的增大,PUE的玻璃化转变温度逐渐降低,耐热性能逐渐增强,损耗因子降低.当NDI/MDI的质量比为1/1 时,PUE在常温和高温下的综合力学性能表现最好.
采用高压发泡机制备了HFC-245fa/水发泡的预制直埋保温管道硬质聚氨酯泡沫.考察了HFC-245fa用量对聚氨酯硬泡压缩强度、导热系数、闭孔率、吸水率、老化前后尺寸稳定性能的影响.结果表明,加入HFC-245fa的聚氨酯硬泡各项性能均比未加入的泡沫好;随着HFC-245fa用量的增加,聚氨酯硬泡各项性能也呈现递增趋势;HFC-245fa用量为零(全水)的泡沫老化前后导热系数变化最大,且HFC-245fa用量越高,老化前后的导热系数差异越小.