Recent developments in "water-in-salt" electrolytes have precipitated a renewed effort to study imide-based electrolytes. While previous small-/wide-angle X-ray scattering (SAXS/WAXS) studies have attributed the emergence of a low-Q peak in the SAXS profile of aqueous LiTFSI electrolytes to nanometer-scale anion clustering, a molecular-level understanding of the root of these clusters remains unclear. In this study, we combined molecular dynamics simulations and SAXS/WAXS to study the solvation structures of LiTFSI in acetonitrile, methanol, and water. We concluded that hydrogen bonding in water and MeOH stabilizes anion clusters, while nonpolar methyl groups on methanol and acetonitrile interrupt the nanoscale ordering of TFSI anions. This causes LiTFSI in water and MeOH electrolytes to exhibit two low-Q SAXS profile peaks while LiTFSI in acetonitrile exhibits only a single peak below Q = 1 & Aring;-1. These findings shed light on the underlying molecular origins of nanoscale anion clusters, which may help in the design of the next generation of electrolyte chemistries.

Electrolyte design is critical for enabling next-generation batteries with higher energy densities. Hydrofluoroether (HFE) solvents have drawn a lot of attention as the electrolytes based on HFEs showed great promise to deliver highly desired properties, including high oxidative stability, ionic conductivity, as well as enhanced lithium metal compatibility. However, the structure-dynamics-properties relationships and design principles for high-performance HFE solvents are still poorly understood. Herein, we proposed four novel asymmetric HFE designs by systematically varying polyether and fluorocarbon structural building blocks. By leveraging molecular dynamics (MD) modeling to analyze the solvation structures and predict the properties of the corresponding 1 M lithium bis(fluorosulfonyl)imide (LiTFSI) solutions, we downselected the most promising candidate based on high conductivity, solvation species distribution, and oxidative stability for extensive electrochemical characterizations. The formulated electrolyte demonstrated properties consistent with the predictions from the simulations and showed much-improved capacity retention as well as Coulombic efficiency compared to the baseline electrolytes when cycled in lithium metal cells. This work exemplifies the construction of candidate electrolytes from building block functional moieties to engineer fundamental solvation structures for desired electrolyte properties and guide the discovery and rational design of new solvent materials.

Ammonia reforming of light alkane is conventionally employed for HCN production where coproduct H2 is burned for heating owing to the high reaction temperature (1200 °C) of such a highly endothermic process. Here, we show that a Ni3Ga1 intermetallic compound (IMC) catalyst is highly efficient for such a reaction, realizing efficient conversion of C1-C3 alkanes at 575-750 °C. This makes it feasible for on-purpose COx-free H2 production assuming that ammonia, as an H2 carrier, is ubiquitously available from renewable energy. At 650 °C and an alkane/ammonia ratio of 1/2, ethane and propane conversion of ∼20% and methane conversion of 13% were obtained (with nearly 100% HCN selectivity for methane and ethane) over the unsupported Ni3Ga1 IMC, which also shows high stability due to the absence of coke deposition. This breakthrough is achieved by employing a stoichiometric Ni3Ga1 mixed oxalate solid solution as the precursor for the Ni3Ga1 IMC.

Processive hydrogenolysis catalysts, in which a metal nanoparticle (e.g., Pt) embedded at the bottom of a cylindrical silica nanopore can repeatedly cleave polymer chains and produce value-added hydrocarbon products, offer a potential solution for billions of tons of waste plastics. As the chain stays longer near the Pt catalysts, it would have a higher chance of getting cut, and therefore the molecular weight distribution of the product could be affected by the adsorption behavior of virgin chains (long polymers) versus cleaved chains (short polymers) into the nanopores. This work reports a model study to understand the competitive adsorption behavior of the two different molecular weight polymers that are mixed, mimicking the reaction medium in the intermediate stage of the catalytic reaction. This study employs small-angle neutron scattering (SANS), which takes advantage of contrast differences between hydrogenous and deuterated polystyrenes to experimentally observe the relative composition of the two polymers in the silica nanopores. Our results reveal preferential adsorption of longer chains in the silica nanopores, which is consistent with the theoretical prediction in the literature for the case of the enthalpic attraction between polymers and pore walls.

The solvation structure of water-in-salt electrolytes was thoroughly studied, and two competing structures & horbar;anion solvated structure and anion network & horbar;were well-defined in recent publications. To further reveal the solvation structure in those highly concentrated electrolytes, particularly the influence of solvent, methanol was chosen as the solvent for this proposed study. In this work, small-angle X-ray scattering, small-angle neutron scattering, Fourier-transform infrared spectroscopy, and Raman spectroscopy were utilized to obtain the global and local structural information. With the concentration increment, the anion network formed by TFSI- became the dominant structure. Meanwhile, the hydrogen bonds among methanol were interrupted by the TFSI- anion and formed a new connection with them. Molecular dynamic simulations with two different force fields (GAFF and OPLS-AA) are tested, and GAFF agreed with synchrotron small-angle X-ray scattering/wide-angle X-ray scattering (SAXS/WAXS) results well and provided insightful information about molecular/ion scale solvation structure. This article not only deepens the understanding of the solvation structure in highly concentrated solutions, but more importantly, it provides additional strong evidence for utilizing SAXS/WAXS to validate molecular dynamics simulations.

The development of cost-effective and highly efficient electrocatalysts is critical to help electrochemical non-enzymatic sensors achieve high performance. Here, a new class of catalyst, Ru single atoms confined on Cu nanotubes as a single-atom alloy (Ru1Cu NTs), with a unique electronic structure and property, was developed to construct a novel electrochemical non-enzymatic glucose sensor for the first time. The Ru1Cu NTs with a diameter of about 24.0 nm showed a much lower oxidation potential (0.38 V) and 9.0-fold higher response (66.5 μA) current than Cu nanowires (Cu NWs, oxidation potential 0.47 V and current 7.4 μA) for glucose electrocatalysis. Moreover, as an electrochemical non-enzymatic glucose sensor, Ru1Cu NTs not only exhibited twofold higher sensitivity (54.9 μA mM−1 cm−2) and wider linear range (0.5–8 mM) than Cu NWs, but also showed a low detection limit (5.0 μM), excellent selectivity, and great stability. According to theoretical calculation results, the outstanding catalytic and sensing performance of Ru1Cu NTs could be ascribed to the upshift of the d-band center that helped promote glucose adsorption. This work presents a new avenue for developing highly active catalysts for electrochemical non-enzymatic sensors.

Graphite is the preferred anode material in commercial lithium-ion batteries (LIBs), but its limited compatibility with various organic molecules restricts the electrolyte solvent options. The primary challenge is solvent co-intercalation with Li ions, leading to graphite layer exfoliation. As a result, electrolyte selection often relies on ethylene carbonate (EC)-based solvents. In this study, we introduce electrolytes featuring a nanoscale anion network ordering that hinders the liquid-phase exfoliation of graphite. This network, formed from concentrated long-chain lithium salts, traps free dioxolane (DOL) molecules, reducing the interactions between graphite particles and solvents during Li intercalation. Our findings reveal a mechanism that stabilizes graphite in otherwise unstable solvents with concentrated salts like LiTFSI, providing key insights for improving LIB performance by addressing electrolyte limitations on graphite anodes.

Redox-active molecules, or redoxmers, in nonaqueous redox flow batteries often suffer from membrane crossover and low electrochemical stability. Transforming inorganic polyionic redoxmers established for aqueous batteries into nonaqueous candidates is an attractive strategy to address these challenges. Here we demonstrate such tailoring for hexacyanoferrate (HCF) by pairing the anions with tetra-n-butylammonium cation (TBA(+)). TBA(3)HCF has good solubility in acetonitrile and >1 V lower redox potential vs the aqueous counterpart; thus, the familiar aqueous catholyte becomes a new nonaqueous anolyte. The lowering of redox potential correlates with replacement of water by acetonitrile in the solvation shell of HCF, which can be traced to H-bond formation between water and cyanide ligands. Symmetric flow cells indicate exceptional stability of HCF polyanions in nonaqueous electrolytes and Nafion membranes completely block HCF crossover in full cells. Ion pairing of metal complexes with organic counterions can be effective for developing promising redoxmers for nonaqueous flow batteries.

Large numbers of leaves fall on the earth each autumn. The current treatments of dead leaves mainly involve completely destroying the biocomponents, which causes considerable energy consumption and environmental issues. It remains a challenge to convert waste leaves into useful materials without breaking down their biocomponents. Here, we turn red maple dead leaves into an active three-component multifunctional material by exploiting the role of whewellite biomineral for binding lignin and cellulose. Owing to its intense optical absorption spanning the full solar spectrum and the heterogeneous architecture for effective charge separation, films of this material show high performance in solar water evaporation, photocatalytic hydrogen production, and photocatalytic degradation of antibiotics. Furthermore, it also acts as a bioplastic with high mechanical strength, high-temperature tolerance, and biodegradable features. These findings pave the way for the efficient utilization of waste biomass and innovations of advanced materials.

The shuttle effects and the sluggish redox kinetics are two of the main challenges in lithium-sulfur (Li-S) batteries, which significantly reduce the capacity of the batteries and restrict their commercialization. Herein, FeCo/ sulfurized polyacrylonitrile (SPAN) is synthesized as a cathode material via the electrospinning technique and a further heat treatment. Synchrotron X-ray absorption spectroscopy confirmed the existence of Fe-S/Fe and Co-S bonds in FeCo/SPAN, which benefit the adsorptive and catalytic activities toward lithium polysulfides (LiPSs). We further investigated the effect of electrolyte concentration in inhibiting the shuttle of LiPSs in Li-S batteries. Small-angle X-ray scattering (SAXS) reveals that more contact ion pairs are formed and fewer free solvent molecules exist with the increase of the electrolyte concentration, which can inhibit the dissolution and shuttle of LiPSs. Finally, the batteries assembled with high concentration electrolytes (3 M LiTFSI in DOL/DME) exhibit a higher specific capacity retention compared to those assembled with low-concentration electrolytes. This work enriches the route to prepare Li-S batteries with the rational design of cathode materials and electrolytes.

The fundamental understanding of the liquid electrolyte (LE) solvation structure and electrode-electrolyte interface behavior will bring more in-depth thinking and revolutionary changes to the entire electrochemical energy storage field. Regardless of the variety of techniques available, the methods employed to investigate electrolyte solvation structures over a long-range are severely limited. Small-angle X-ray scattering (SAXS) is an ideal complement to Raman spectroscopy, Fourier transform infrared spectroscopy, or nuclear magnetic resonance, which offers a unique perspective from a larger scale on clusters or networks in electrolytes. Understanding the solvation structures from a few angstroms to hundreds of nanometers will undoubtedly lay a good foundation for studying the macroscopic transport properties, such as viscosity and ionic conductivity, of the LEs. In this Perspective, we discuss the use of SAXS to investigate the solvation structures in different electrolyte systems, a prospect for the SAXS broader application in the electrolyte study, and some challenges that need to be solved in the SAXS application.

Lithium-ion batteries (LIBs) currently dominate the energy storage market for electronic devices, thanks to their high energy density, high operating voltage, and good cycling performance. However, commercial LIBs employing organic liquid electrolyte and lithium (Li) salts pose significant safety concerns, including flammability and the risk of thermal runaway. Consequently, the development of solid electrolytes is of paramount importance. Among several solid ion conductors, solid polymer electrolytes (SPEs) can offer numerous advantages, including excellent flexibility and interfacial compatibility with electrodes, good processibility, low cost, and light weight characteristics. However, current SPEs face challenges such as poor thermal stability, inferior electrochemical stability, and low Li-ion conductivity at room temperature (~ 10 -5 S cm -1 at 25 ℃). In this study, we introduce a multifunctional zwitterionic polyurethane-based solid polymer electrolyte (zPU-SPE) for all-solid-state LIBs (SLBs) that addresses the limitations of conventional SPE materials. We synthesized zPU [i.e., poly((diethanolamine ethyl acetate)-co-poly(tetrahydrofuran)-co-(1,6-diisocyanatohexane))] and demonstrated its capability to host high amounts of LiTFSI without phase separation (up to 90 wt% LiTFSI loading). The Li-ion conductivity of zPU-SPE at 25° C is 7.4 × 10 -4 S/cm, nearly 14 times greater than that of poly(ethylene oxide) (PEO) SPE (EO/Li + = 16). Moreover, the high surface energy of zPU-SPE (487.5 J/m 2 vs. 1.39 J/m 2 of PEO) minimizes interfacial resistance. The zPU-SPE also exhibits outstanding elasticity, with a tensile break of 1700%, attributable to its dense inter- and intra-molecular hydrogen bonding. We evaluated the SLB battery performance of PEO and zPU-SPEs using a solid-state Li/SPE/LiFePO 4 cell, which we cycled at a constant current rate of 1 C at 25 °C. The SLB cell with zPU-SPE demonstrates remarkable cycle stability, retaining 86% capacity after 1,000 cycles and 76% capacity after 2,000 cycles at a 1C rate and room temperature, while maintaining nearly 100% coulombic efficiency. In contrast, the capacity of the SLB cell with PEO rapidly decreases to 30% of its initial capacity and fails after 100 cycles. Given that significant capacity loss in LIBs under cold weather conditions poses a challenge for electric vehicles, we also assessed the temperature-dependent battery performance. The SLB with zPU-SPE retains 93.8% capacity at 0 °C, a substantial improvement over state-of-the-art LIBs (< 80% capacity retention). We attribute the high-capacity retention of zPU-SPE at low temperatures to the excellent chain mobility of the soft segment in the zPU matrix, which has a low glass transition temperature (-45 °C) and a high ion transport rate due to the zwitterionic group. We also conducted atomistic molecular modeling to investigate the dissolution and dissociation of Li salts and the Li-ion transport mechanism within the zPU polymer matrix. Furthermore, we employed small-angle X-ray scattering to examine the structural organization of the zPU-SPE matrix and its correlation with ion conductivity. Our work aims to guide the design of novel polymer electrolytes capable of overcoming the trade-offs associated with ion-conducting polymers (i.e., stability and ion conductivity). Figure 1

The mesoporous silica shell coating hydrogenolysis nano-catalysts alters the molecular weight distributions of cleaved polymer chains compared to catalysts without a shell. The shell, composed of radially aligned narrow cylindrical nanopores, reduces the formation of low-valued gaseous products and increases the median molecular weight of the product, thus enhancing the value of the products for polymer upcycling. To understand the role of the mesoporous shell, we have studied the spatial distribution of polystyrene chains, used as a model polymer, in the nanochannels in both the melt phase and solution phase. In the melt, we observed from small-angle X-ray scattering experiments that the infiltration rate of the polymer into the nanochannels is inversely proportional to the molecular weight, which is consistent with theory. In theta solution experiments using UV-vis spectroscopy, we found that the shell significantly enhances polymer adsorption compared to nanoparticles without pores. In addition, the degree of polymer adsorption is not a monotonic function of molecular weight but initially increases with the molecular weight before eventually decreasing. The molecular weight for the peak adsorption increases with the pore diameter. This adsorption behavior is rationalized as resulting from a balance between the mixing entropy gain by surface adsorption and the conformational entropy penalty incurred by chains confined in the nanochannels. The spatial distribution of polymer chains in the nanochannels is visualized by energy-dispersive X-ray spectroscopy (EDX), and inverse Abel-transformed data reveals a less uniform polymer distribution along the primary pore axis for longer chains.

PbS quantum dots (QDs) are promising building blocks for solution-processed short-wavelength infrared (SWIR) devices. The recently developed direct synthesis of semi-conductive PbS QD inks has substantially simplified the preparation processing and reduced the material cost, while facing the challenge to synthesize large-size QDs with absorption covering the SWIR region. Herein, we for the first time realize a low-cost, scalable synthesis of SWIR PbS QD inks after an extensive investigation of the reaction kinetics. Finally, based on these PbS SWIR QD inks, the solar cell demonstrates a record-high power conversion efficiency (PCE) of 1.44 % through an 1100 nm cutoff silicon filter and the photodetector device shows a low dark current density of 2×10 −6  A cm −2 at −0.8 V reverse bias with a high external quantum efficiency (EQE) of 70 % at ≈1300 nm. Our results realize the direct synthesis of low-cost and scalable SWIR QD inks and may accelerate the industrialization of consumer SWIR technologies.

The development of novel single-atom catalysts is important for highly efficient electrochemical catalysis and sensing. In this work, a novel Pt single atoms (SAs) supported on Ni 6 Co 1 layered double hydroxides/nitrogen-doped graphene (Pt 1 /Ni 6 Co 1 LDHs/NG) was constructed for electrochemical enzyme-free catalysis and sensing towards glucose. The loading of Pt single atoms increases with doping of Co atoms that generate more anchoring sites for Pt SAs. The resulting Pt 1 /Ni 6 Co 1 LDHs/NG exhibits low oxidative potential of 0.440 V with high sensitivity of 273.78 µA·mM −1 ·cm −2 toward glucose, which are 85 mV lower and 15 times higher than those of Ni(OH) 2 , respectively. Pt 1 /Ni 6 Co 1 LDHs/NG also shows excellent selectivity and great stability during 5-week testing. Theoretical and experimental results show that the boosted performance of Pt 1 /Ni 6 Co 1 LDHs/NG originates from its stronger binding energy with glucose and the synergistic effect of Pt SAs, Co doping, and NG. This work provides a general strategy of designing highly active SACs for extending their application in electrochemical sensing.

Tin-based electrocatalysts exhibit a remarkable ability to catalyze CO2 to formate selectively. Understanding the size-property relationships and exploring the evolution of the active size still lack complete understanding. Herein, we prepared SnO2 nanoparticles (NPs) with a controllable size supported on commercial carbon spheres (SnO2/C-n, n = 1, 2, and 3) by a simple low-temperature annealing method. The transmission electron microscopy/scanning transmission electron microscopy images and fitting results of the small-angle X-ray scattering profile confirm the increased size of SnO2 NPs due to the increase of SnO2 loading. The catalytic performance of SnO2 has proved the size-dependent effect during the CO2 reduction reaction process. The as-prepared SnO2/C-1 displayed the maximum Faradic efficiency of formate (FEHCOO-) of 82.7% at -1.0 V versus reversible hydrogen electrode (RHE). In contrast, SnO2/C-2 and SnO2/C-3 with larger particle sizes achieved lower maximum FEHCOO- and larger overpotential. Moreover, we employed operando X-ray absorption spectroscopy to study the evolution of the oxidation state and local coordination environment of SnO2 under working conditions. In addition to the observed shifts of the rising edge of Sn K-edge X-ray absorption near-edge structure spectra to a lower energy side as the applied voltage decreases, the decreased coordination number of Sn in the Sn-O scattering path and the presence of Sn metal contribution in the extended X-ray absorption fine structure spectra verify the reduction of SnO2 to SnOx and metallic Sn.

Realization of practical sodium metal batteries (SMBs) is hindered due to lack of compatible electrolyte components, dendrite propagation, and poor understanding of anodic interphasial chemistries. Chemically robust liquid electrolytes that facilitate both favorable sodium metal deposition and a stable solid-electrolyte interphase (SEI) are ideal to enable sodium metal and anode-free cells. Herein we present advanced characterization of a novel fluorine-free electrolyte utilizing the [HCB11H11](1-) anion. Symmetrical Na cells operated with this electrolyte exhibit a remarkably low overpotential of 0.032 V at a current density of 2.0 mA cm(-2) and a high coulombic efficiency of 99.5 % in half-cell configurations. Surface characterization of electrodes post-operation reveals the absence of dendritic sodium nucleation and a surprisingly stable fluorine-free SEI. Furthermore, weak ion-pairing is identified as key towards the successful development of fluorine-free sodium electrolytes.

Coating the catalyst with a nanoporous layer has been demonstrated to be an effective approach to improve catalyst stability. Herein, we systematically investigate two types of core-shell mesoporous silica nanoparticles with a platinum nanocatalyst using a variety of characterization methods. One of the mesoporous particles has a unique amine ring structure in the middle of a shell (Ring-mSiO2/Pt-5.0/SiO2), and the other one has no ring structure (mSiO2/Pt-5.0/SiO2). Brunauer–Emmett–Teller/Barrett–Joyner–Halenda (BET/BJH) presented a similar surface area for both particles, and the pore size was 2.4 nm. Ultra-Small-Angle X-ray Scattering (USAXS)/ Small-Angle X-ray Scattering (SAXS) showed the size of mSiO2/Pt-5.0/SiO2 and Ring-mSiO2/Pt-5.0/SiO2 were 420 nm and 272 nm, respectively. It also showed that the ring structure was 30 nm above the silica core. Using high-resolution Transmission Electron Microscopy (TEM), it was found that the platinum nanoparticles are loaded evenly on the surface of the silica. In situ SAXS heating experiments and Thermogravimetric Analysis (TGA) indicated that the mSiO2/Pt-5.0/SiO2 were more stable during the high temperature, while the Ring-mSiO2/Pt-5.0/SiO2 had more change in the particle.

Enzymes are the highly efficient biocatalyst in modern biotechnological industries. Due to the fragile property exposed to the external stimulus, the application of enzymes is highly limited. The immobilized enzyme by polymer has become a research hotspot to empower enzymes with more extraordinary properties and broader usage. Compared with free enzyme, polymer immobilized enzymes improve thermal and operational stability in harsh environments, such as extreme pH, temperature and concentration. Furthermore, good reusability is also highly expected. The first part of this study reviews the three primary immobilization methods: physical adsorption, covalent binding and entrapment, with their advantages and drawbacks. The second part of this paper includes some polymer applications and their derivatives in the immobilization of enzymes.

Intelligent control of friction and adhesion has attracted much attention for use in soft robotics, human-sensor interfaces, and bionics. Here we introduce a shape memory photonic crystal (SMPC) polymer that can be programmed and recovered by solvent to realize switchable surface friction. Micro sliding test show that the friction coefficient on this SMPC in the programmed and recovered state can vary by three times. We also show that the mechanism behind this switchable friction coefficient is the surface roughness related adhesion.